TPV SARLINK® 5775B TEKNOR APEX BELGIUM
So sánhBảng thông số kỹ thuật
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 1.5mm | UL 94 | HB |
| elastomer | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| tensile strength | tensile strength 横向Flow:100%Strain | ASTM D412 | 3.20 Mpa |
| tensile strength | tensile strength Flow:100%Strain | ASTM D412 | 4.90 Mpa |
| tensile strength | tensile strength 横向Flow:100%Strain | ISO 37 | 3.20 Mpa |
| tensile strength | tensile strength Flow:100%Strain | ISO 37 | 4.90 Mpa |
| tensile strength | tensile strength Break | ASTM D412 | 8.48 Mpa |
| tensile strength | tensile strength Flow:Break | ASTM D412 | 7.31 Mpa |
| tensile strength | tensile strength Break | ISO 37 | 8.50 Mpa |
| tensile strength | tensile strength Flow:Break | ISO 37 | 7.30 Mpa |
| elongation | elongation Break | ASTM D412 | 590 % |
| elongation | elongation Flow:Break | ASTM D412 | 340 % |
| elongation | elongation Break | ISO 37 | 590 % |
| elongation | elongation Flow:Break | ISO 37 | 340 % |
| tear strength | tear strength 横向Flow | ASTM D624 | 35.0 kN/m |
| tear strength | tear strength 横向Flow | ISO 34-1 | 35 kN/m |
| Permanent compression deformation | Permanent compression deformation 23°C,22hr | ASTM D395 | 23 % |
| Permanent compression deformation | Permanent compression deformation 70°C,22hr | ASTM D395 | 32 % |
| Permanent compression deformation | Permanent compression deformation 125°C,70hr | ASTM D395 | 47 % |
| Permanent compression deformation | Permanent compression deformation 23°C,22hr | ISO 815 | 23 % |
| Permanent compression deformation | Permanent compression deformation 70°C,22hr | ISO 815 | 32 % |
| Permanent compression deformation | Permanent compression deformation 125°C,70hr | ISO 815 | 47 % |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| RTI Elec | RTI Elec | UL 746 | 50.0 °C |
| RTI Imp | RTI Imp | UL 746 | 50.0 °C |
| RTI Str | RTI Str | UL 746 | 50.0 °C |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Shore hardness | Shore hardness ShoreA,5Sec,挤塑 | ASTM D2240 | 72 |
| Shore hardness | Shore hardness ShoreA,5Sec,Injection | ASTM D2240 | 75 |
| Shore hardness | Shore hardness ShoreA,5Sec,挤塑 | ISO 868 | 72 |
| Shore hardness | Shore hardness ShoreA,5Sec,Injection | ISO 868 | 75 |
| aging | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Change rate of hardness (Shore) in the air | Change rate of hardness (Shore) in the air ShoreA,135°C,1000hr | ASTM D573 | 3.0 |
| Change rate of hardness (Shore) in the air | Change rate of hardness (Shore) in the air ShoreA,150°C,168hr | ASTM D573 | 2.0 |
| Change rate of hardness (Shore) in the air | Change rate of hardness (Shore) in the air ShoreA,135°C,1000hr | ISO 188 | 3.0 |
| Change rate of hardness (Shore) in the air | Change rate of hardness (Shore) in the air ShoreA,150°C,168hr | ISO 188 | 2.0 |
| Volume change | Volume change 125°C,70hr,在IRM903油中 | ASTM D471 | 88 % |
| Volume change | Volume change 125°C,70hr,在IRM903油中 | ISO 1817 | 88 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 150°C,168hr，Across Flow | ASTM D573 | -10 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 100%Strain,150°C,168hr，Across Flow | ASTM D573 | 2.0 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 135°C,1000hr，Across Flow | ISO 188 | -8.0 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 100%Strain135°C,1000hr，Across Flow | ISO 188 | 4.0 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 150°C,168hr，Across Flow | ISO 188 | -10 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 100%Strain150°C,168hr，Across Flow | ISO 188 | 2.0 % |
| Change rate of ultimate elongation in air | Change rate of ultimate elongation in air 135°C,1000hr，Across Flow | ASTM D573 | -7.0 % |
| Change rate of ultimate elongation in air | Change rate of ultimate elongation in air 150°C,168hr，Across Flow | ASTM D573 | -11 % |
| Tensile stress change rate | Tensile stress change rate 135°C,1000hr，Break | ISO 188 | -7.0 % |
| Tensile stress change rate | Tensile stress change rate 150°C,168hr，Break | ISO 188 | -11 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 135°C,1000hr，Across Flow | ASTM D573 | -8.0 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 100%Strain,135°C,1000hr，Across Flow | ASTM D573 | 4.0 % |
| Supplementary Information | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Apparent viscosity | Apparent viscosity 200°C，剪切,毛细管法, @206/s | ISO 11443 | 330 Pa·s |
| Apparent viscosity | Apparent viscosity 200°C，剪切,毛细管法, @206/s | ASTM D3835 | 330 Pa·s |