PBT+ASA POCAN® TP 740-101 000000 LANXESS GERMANY

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	40 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	50 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	40 kJ/m²

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Impact strength of simply supported beam without notch

-30°C

ISO 179/1eU

40 kJ/m²

Impact strength of simply supported beam without notch

23°C

ISO 179/1eU

50 kJ/m²

Suspended wall beam without notch impact strength

23°C

ISO 180/1U

40 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

0.8mm

UL 94

UL flame retardant rating

1.6mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	2.5 %
Bending modulus	Bending modulus 23°C	ISO 178/A	5200 MPa
bending strength	bending strength 23°C	ISO 178/A	150 MPa
Bending strain	Bending strain 23°C	ISO 178/A	3.2 %
Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	6000 MPa
tensile strength	tensile strength Break,23°C	ISO 527-2/5	100 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	210 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	150 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B120	165 °C
Melting temperature	Melting temperature	ISO 11357-3	225to250 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 270°C/5.0kg	ISO 1133	55.0 cm³/10min
Shrinkage rate	Shrinkage rate TD:270°C,2.00mm2	ISO 2577	0.70 %
	Shrinkage rate	Shrinkage rate TD:120°C,4hr,2.00mm3	ISO 2577	0.30 %
		Shrinkage rate	Shrinkage rate MD:270°C,2.00mm2	ISO 2577	0.40 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD:120°C,4hr,2.00mm3	ISO 2577	0.20 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.40 %
density	density 23°C	ISO 1183	1.39 g/cm³
Apparent density	Apparent density	ISO 60	0.80 g/cm³
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.10 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	150 MPa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

ISO 2039-1

150 MPa

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ISO Shortcut	ISO Shortcut	ISO 7792	PBT+PET+ASA.GHMR.09-060.GF15

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

ISO Shortcut

ISO 7792

PBT+PET+ASA.GHMR.09-060.GF15

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.