	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.22 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 260°C/5.0kg	ISO 1133	16.0 cm³/10min
Shrinkage rate	Shrinkage rate	ISO 294-4	0.20to0.60 %
Tensile modulus	Tensile modulus	ISO 527-2/1	3700 MPa
tensile strength	tensile strength Yield	ISO 527-2/50	46.0 MPa
tensile strength	tensile strength	tensile strength Break	ISO 527-2/5	45.0 MPa
Tensile strain	Tensile strain Yield	ISO 527-2/50	5.0 %
Nominal tensile fracture strain	Nominal tensile fracture strain	ISO 527-2/50	5.0 %
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	4.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	20 kJ/m²
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	104 °C
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.