mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Environmental stress cracking resistance	Environmental stress cracking resistance 10% Igepal，F50	ASTM D-1693B	>500 hr
Environmental stress cracking resistance	Environmental stress cracking resistance	Environmental stress cracking resistance 100% Igepal，F50	ASTM D-1693B	1000 hr
tensile strength	tensile strength Yield	ASTM D-638	17.2 MPa
Elongation at Break	Elongation at Break	ASTM D-638	780 %
Bending modulus	Bending modulus	ASTM D-790	760 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa，Unannealed	ASTM D-648	39.5 ℃
Vicat softening temperature	Vicat softening temperature	ASTM D-1525	112 ℃
Hot deformation temperature	Hot deformation temperature 0.45MPa，Unannealed	ASTM D-648	53 ℃

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Hot deformation temperature

1.8MPa，Unannealed

ASTM D-648

39.5 ℃

Vicat softening temperature

ASTM D-1525

112 ℃

Hot deformation temperature

0.45MPa，Unannealed

ASTM D-648

53 ℃

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.