PCT Infino TK-2050H LOTTE KOREA
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength -5°C5 | ISO 180/1U | 11 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C,6.35mm | ASTM D256 | 170 J/m |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C,3.18mm | ASTM D256 | 170 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C5 | ISO 180/1A | 3.0 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C,6.35mm | ASTM D256 | 22 J/m |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 2.7 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | 12 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C,3.18mm | ASTM D256 | 23 J/m |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 3.0mm | UL 94 | HB |
| UL flame retardant rating | UL flame retardant rating 1.5mm | UL 94 | HB |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| tensile strength | tensile strength Yield3 | ASTM D638 | 58.8 MPa |
| Tensile modulus | Tensile modulus -- | ISO 527-2/5 | 6050 MPa |
| Tensile modulus | Tensile modulus --3 | ASTM D638 | 4780 MPa |
| Bending modulus | Bending modulus -- | ASTM D790 | 6370 MPa |
| elongation | elongation Break | ISO 527-2/5 | 1.7 % |
| tensile strength | tensile strength Yield | ISO 527-2/5 | 57.0 MPa |
| tensile strength | tensile strength Break3 | ASTM D638 | 58.8 MPa |
| tensile strength | tensile strength Break | ISO 527-2/5 | 57.0 MPa |
| elongation | elongation Break3 | ASTM D638 | 2.1 % |
| Bending modulus | Bending modulus -- | ISO 178 | 6960 MPa |
| bending strength | bending strength -- | ASTM D790 | 71.6 MPa |
| bending strength | bending strength -- | ISO 178 | 74.0 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,4.00mm | ISO 75-2/A | 203 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,6.40mm | ASTM D648 | 240 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed,4.00mm | ISO 75-2/B | 240 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Shrinkage rate | Shrinkage rate MD:3.20mm | ASTM D955 | 0.49to0.59 % |
| melt mass-flow rate | melt mass-flow rate 300°C/2.16kg | ASTMD1238 | 35 g/10min |
| ash content | ash content -- | ISO 3451 | 51 % |
| ash content | ash content -- | ASTM D5630 | 51 % |
| Shrinkage rate | Shrinkage rate MD:3.20mm | ISO 2577 | 0.49to0.59 % |
| Shrinkage rate | Shrinkage rate TD:3.20mm | ISO 2577 | 0.50to0.62 % |
| Shrinkage rate | Shrinkage rate TD:3.20mm | ASTM D955 | 0.50to0.62 % |
| density | density | ASTMD792 | 1.79 g/cm³ |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Rockwell hardness | Rockwell hardness R-Sale | ISO 2039-2 | 119 |
| Rockwell hardness | Rockwell hardness R-Scale | ASTM D785 | 119 |