Ethylene Copolymer Lushan EV1050G1/RF Guangzhou Lushan New Materials Co., Ltd

So sánh

Bảng thông số kỹ thuật

	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	ASTM D150	>1.0E+14 ohms·cm
adhesion	adhesion toglass	ASTM D903	>10.0 kN/m
adhesion	adhesion	adhesion tobacksheet	ASTM D903	>8.0 kN/m
UVCutoff-Wavelength	UVCutoff-Wavelength	Internal Method	360 nm
Refractive index	Refractive index	ISO 489	1.490
Melting temperature	Melting temperature	ASTM D148	65.0to75.0 °C
elongation	elongation Break	ISO 527-3	>400 %
tensile strength	tensile strength	ISO 527-3	25.0 MPa
Tensile modulus	Tensile modulus	ISO 527-3	8.00 MPa
Gel content	Gel content	Internal Method	>80 %
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	<0.10 %
Shrinkage rate	Shrinkage rate TD:120°C	Internal Method	0.0 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD:120°C	Internal Method	0.0 %
melt mass-flow rate	melt mass-flow rate	ASTM D1238	17to27 g/10min
density	density	ISO 1183	0.960 g/cm³

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.