PA66 Vydyne® 22HSP NT Ascend Performance Materials Operations LLC

So sánh

Bảng thông số kỹ thuật

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	NB kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	5.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	6.0 kJ/m²
Bending modulus	Bending modulus 23°C	ISO 178	2900 MPa
bending strength	bending strength 23°C	ISO 178	95 MPa
Tensile modulus	Tensile modulus 泊松比	ISO 527-2	0.40
Tensile modulus	Tensile modulus	Tensile modulus 23°C	ISO 527-2	3100 MPa
Elongation at Break	Elongation at Break 23°C	ISO 527-2	25 %
Elongation at Break	Elongation at Break	Elongation at Break Yield,23°C	ISO 527-2	5.0 %
tensile strength	tensile strength 23°C	ISO 527-2	55 MPa
tensile strength	tensile strength	tensile strength Yield,23°C	ISO 527-2	85 MPa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	5.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	NB kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	6.0 kJ/m²

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion 熔点	ISO 11359-2	260 °C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	1E-05 cm/cm／°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	1E-05 cm/cm／°C
Hot deformation temperature	Hot deformation temperature 1.80MPaAnnealed	ISO 75-2/Af	70 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPaUnannealed	ISO 75-2/Bf	200 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate (23°C,50RH)	ISO 62	2.4 %
Water absorption rate	Water absorption rate	Water absorption rate (23°C,24hr)	ISO 62	1.2 %
Shrinkage rate	Shrinkage rate MD2.0mm	ISO 294-4	2.0 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD2.0mm	ISO 294-4	2.2 %
density	density	ISO 1183	1.14 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 相对漏电起痕指数	IEC 60112	400-599 V
Dissipation factor	Dissipation factor 耐电弧性	IEC 61621	60-119 s

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Dissipation factor

相对漏电起痕指数

IEC 60112

400-599 V

Dissipation factor

耐电弧性

IEC 61621

60-119 s

flame retardant performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	23 %
UL flame retardant rating	UL flame retardant rating	UL -94	V-2 3.00mm
	UL flame retardant rating	UL flame retardant rating	UL -94	V-2 1.50mm
	UL flame retardant rating	UL flame retardant rating	UL flame retardant rating	UL -94	V-2 0.71mm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.