impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	400 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ISO 180/1A	12 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	14 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	14 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	15 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Burning rate	Burning rate 1.00mm	ISO 3795	50 mm/min
UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating 0.8mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 1.5mm	IEC 60695-11-10,-20	HB
FMVSS flammability	FMVSS flammability	FMVSS302	B
Atomization	Atomization refraction，F值	ISO 6452	91 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2	2950 Mpa
tensile strength	tensile strength Yield	ISO 527-2	71.0 Mpa
Tensile strain	Tensile strain Yield	ISO 527-2	25 %
Nominal tensile fracture strain	Nominal tensile fracture strain	ISO 527-2	45 %
Tensile creep modulus	Tensile creep modulus 1hr	ISO 899-1	2700 Mpa
Tensile creep modulus	Tensile creep modulus	Tensile creep modulus 1000hr	ISO 899-1	1500 Mpa
Bending modulus	Bending modulus	ISO 178	2850 Mpa
bending strength	bending strength 3.5%Strain	ISO 178	77.0 Mpa
Poisson's ratio	Poisson's ratio	ISO 527	0.35

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melting temperature	Melting temperature	ISO 11357-3	178 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：--	ISO 11359-2	1.1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to23°C	ISO 11359-2	1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：--	ISO 11359-2	1.1E-04 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to23°C	ISO 11359-2	1E-04 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：AnnealingTemperature	ISO 11359-2	160 °C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：AnnealingTime-Optional	ISO 11359-2	30.0 min/mm
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	155 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	95.0 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	175 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	160 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.42 g/cm³
melt mass-flow rate	melt mass-flow rate	ISO 1133	2.6 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 190°C/2.16kg	ISO 1133	2.20 cm3/10min
Shrinkage rate	Shrinkage rate TD	ISO 294-4	1.9 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	2.2 %
Water absorption rate	Water absorption rate Saturation,23°C,2.00mm	ISO 62	1.4 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.30 %
MediumDensity	MediumDensity		1.19 g/cm³
SpecificHeatCapacity of Melt	SpecificHeatCapacity of Melt		3000 J/kg/°C
ThermalConductivityofMelt	ThermalConductivityofMelt		0.22 W/m/K

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 60093	2E+13 ohms
Volume resistivity	Volume resistivity	IEC 60093	1E+14 ohms·cm
Dielectric strength	Dielectric strength	IEC 60243-1	41 KV/mm
Relative permittivity	Relative permittivity 100Hz	IEC 60250	3.90
Relative permittivity	Relative permittivity	Relative permittivity 1MHz	IEC 60250	3.90
Dissipation factor	Dissipation factor 100Hz	IEC 60250	3.5E-03
Dissipation factor	Dissipation factor	Dissipation factor 1MHz	IEC 60250	5.5E-03
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	V

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness M-Sale	ISO 2039-2	88
Rockwell hardness	Rockwell hardness R-Sale	ISO 2039-2	119

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

M-Sale

ISO 2039-2

Rockwell hardness

R-Sale

ISO 2039-2

119

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Emission	Emission	VDA275	<8.00 mg/kg
EmissionofOrganicCompounds	EmissionofOrganicCompounds	VDA277	4.70 µgC/g

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Emission

VDA275

<8.00 mg/kg

EmissionofOrganicCompounds

VDA277

4.70 µgC/g

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.