mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rubbing modulus	Rubbing modulus 23℃	ASTM D-790	207 Mpa
Elongation at Break	Elongation at Break Break	ASTM D-638	40 Mpa
Initial tear strength	Initial tear strength	ASTM D-1004	158 kN/m
Elongation at Break	Elongation at Break	ASTM D-638	500 %
tensile strength	tensile strength 10%伸长	ASTM D-638	10.3 Mpa
tensile strength	tensile strength	tensile strength 5%伸长	ASTM D-638	6.9 Mpa
Shore hardness	Shore hardness	ASTM D-2240	55
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃	ASTM D-256	不破裂 J/m

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature @0.18Mpa	ASTM D-648	49 °C
Vicat softening temperature	Vicat softening temperature	ASTM D-1525	180 °C
Melting temperature	Melting temperature	ASTM D-3418	203 °C

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Hot deformation temperature

@0.18Mpa

ASTM D-648

49 °C

Vicat softening temperature

ASTM D-1525

180 °C

Melting temperature

ASTM D-3418

203 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Taber abraser	Taber abraser CS-17轮	ASTM D-1044	6 mg/1000rev
Taber abraser	Taber abraser	Taber abraser H 18轮	ASTM D-1044	64 mg/1000rev
melt mass-flow rate	melt mass-flow rate	ASTM D-1238	7.5 g/10min
Hot deformation temperature	Hot deformation temperature @0.5Mpa	ASTM D-648	90 °C

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.