PA612 VESTAMID® D DX9321 Altuglas International of Arkema Inc.

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C,Complete Break	ISO 179/1eU	93 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C,Complete Break	ISO 179/1eU	110 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C,Complete Break	ISO 179/1eA	18 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C,Complete Break	ISO 179/1eA	11 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.6mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2/1A	5700 MPa
tensile strength	tensile strength Yield	ISO 527-2/1A	-- MPa
Tensile strain	Tensile strain Break	ISO 527-2/1A	5.0 %
Tensile strain	Tensile strain	Tensile strain Yield	ISO 527-2/1A	-- %
tensile strength	tensile strength Break	ISO 527-2/1A	115 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	ISO 11359-2	7E-05 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	215 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B	207 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	189 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	208 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to55°C	ISO 11359-2	5E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.80 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	2.0 %
Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ISO 294-4	0.90 %
density	density 23°C	ISO 1183	1.19 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA5	IEC 60112	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA4	IEC 60112	PLC 0
Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.047
Dissipation factor	Dissipation factor	Dissipation factor 100Hz	IEC 60250	0.050
Relative permittivity	Relative permittivity 1MHz	IEC 60250	3.10
Volume resistivity	Volume resistivity	IEC 60093	1E+14 ohms·cm
Relative permittivity	Relative permittivity 100Hz	IEC 60250	4.40

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ISO Shortcut	ISO Shortcut	ISO 1874	PA612-HI.MH.14-050.GF20

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

ISO Shortcut

ISO 1874

PA612-HI.MH.14-050.GF20

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.