PBT+PET VALOX™ V8030CS resin SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	24 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	4.1 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	4.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	58 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Fracture bending strain	Fracture bending strain	ISO 178	3.4 %
bending strength	bending strength Break,50.0mmSpan	ASTM D790	148 MPa
tensile strength	tensile strength Yield	ISO 527-2/5	95.0 MPa
tensile strength	tensile strength	tensile strength Yield	ASTM D638	99.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1	5890 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ASTM D638	6180 MPa
tensile strength	tensile strength Break	ASTM D638	98.0 MPa
elongation	elongation Break2	ASTM D638	8.6 %
Tensile strain	Tensile strain Yield	ISO 527-2/5	2.1 %
elongation	elongation Yield	ASTM D638	2.7 %
tensile strength	tensile strength Break	ISO 527-2/5	103 MPa
elongation	elongation Break3	ASTM D638	2.8 %
Tensile strain	Tensile strain Break	ISO 527-2/5	2.0 %
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	5580 MPa
Bending modulus	Bending modulus	Bending modulus	ISO 178	5480 MPa
bending strength	bending strength	ISO 178	148 MPa
bending strength	bending strength	bending strength Yield,50.0mmSpan	ASTM D790	148 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	222 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature	ASTM D15258	224 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	173 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	220 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A120	222 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 265°C/5.0kg	ISO 1133	75.0 cm³/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 265°C/2.16kg	ISO 1133	29.0 cm³/10min
density	density	ISO 1183	1.43 g/cm³
density	density	density	ASTM D792	1.43 g/cm³

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.