impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	95.0 J
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	9.0 kJ/m²

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Dart impact

23°C,TotalEnergy

ASTM D3763

95.0 J

Impact strength of cantilever beam gap

23°C

ISO 180/1A

9.0 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	1840 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	1900 Mpa
tensile strength	tensile strength Yield	ASTM D638	49.0 Mpa
tensile strength	tensile strength	tensile strength Yield	ISO 527-2/50	55.0 Mpa
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	83.0 Mpa
bending strength	bending strength	bending strength	ISO 178	71.0 Mpa
Bending modulus	Bending modulus	ISO 178	2000 Mpa
Bending modulus	Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	1940 Mpa
Tensile strain	Tensile strain Break	ISO 527-2/50	>150 %
elongation	elongation Break	ASTM D638	150 %
Tensile strain	Tensile strain Yield	ISO 527-2/50	5.0 %
elongation	elongation Yield	ASTM D638	5.0 %
tensile strength	tensile strength Break	ISO 527-2/50	55.0 Mpa
tensile strength	tensile strength	tensile strength Break	ASTM D638	52.0 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	1.1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to60°C	ISO 11359-2	8.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to60°C	ISO 11359-2	8.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	1.2E-04 cm/cm/°C
Vicat softening temperature	Vicat softening temperature	ISO 306/B120	106 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature	ASTM D15259	108 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	90.0 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	88.0 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	102 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 265°C/2.16kg	ASTM D1238	21 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 265°C/2.16kg	ISO 1133	21.0 cm3/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.40-0.80 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD：3.20mm	Internal Method	0.50-0.70 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.