flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating 0.75mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

3.0mm

UL 94

V-0

UL flame retardant rating

1.5mm

UL 94

V-1

UL flame retardant rating

0.75mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Taber abraser	Taber abraser 1000Cycles,1000g,CS-17Wheel	ASTM D1044	24.0 mg
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	153 Mpa
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	6610 Mpa
elongation	elongation Break	ASTM D638	2.0 %
tensile strength	tensile strength Break	ASTM D638	100 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
RTI Elec	RTI Elec	UL 746	120 °C
RTI Imp	RTI Imp	UL 746	120 °C
RTI Str	RTI Str	UL 746	130 °C
thermal conductivity	thermal conductivity	ASTMC177	0.22 W/m/K
specific heat	specific heat	ASTMC351	1130 J/kg/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	151 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	146 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15255	165 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to95°C	ASTME831	2.2E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Specific volume	Specific volume	ASTM D792	0.697 cm³/g
Water absorption rate	Water absorption rate Equilibrium,23°C	ASTM D570	0.26 %
Water absorption rate	Water absorption rate	Water absorption rate 24hr	ASTM D570	0.14 %
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.10-0.30 %
melt mass-flow rate	melt mass-flow rate 300°C/5.0kg	ASTM D1238	19 g/10min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ASTM D1238	5.0 g/10min

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	ASTM D257	>1.0E+17 ohms·cm
Hot wire ignition	Hot wire ignition HWI	UL 746	PLC 0
High voltage arc tracing rate	High voltage arc tracing rate HVTR	UL 746	PLC 3
High arc combustion index	High arc combustion index HAI	UL 746	PLC 4
Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 5
Arc resistance	Arc resistance	ASTM D495	PLC7
Dissipation factor	Dissipation factor 1MHz	ASTM D150	7E-03
	Dissipation factor	Dissipation factor 60Hz	ASTM D150	1.1E-03
	Dissipation factor	Dissipation factor	Dissipation factor 50Hz	ASTM D150	1.1E-03
Dielectric strength	Dielectric strength 3.20mm,inAir	ASTM D149	19 KV/mm
Dielectric constant	Dielectric constant 50Hz	ASTM D150	3.35
	Dielectric constant	Dielectric constant 60Hz	ASTM D150	3.35
	Dielectric constant	Dielectric constant	Dielectric constant 1MHz	ASTM D150	3.31

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness M-Sale	ASTM D785	92
Rockwell hardness	Rockwell hardness R-Sale	ASTM D785	120

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

M-Sale

ASTM D785

Rockwell hardness

R-Sale

ASTM D785

120

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.