ABS+PA Novalloy-A A2508 (Type V) DAICEL JAPAN

So sánh

Bảng thông số kỹ thuật

	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
yield	yield		43.03to56.41 Mpa
crack	crack		51.03to124.14 Mpa
elongation	elongation Break,23℃	%	3.8to4.0
Tensile modulus	Tensile modulus 23℃		2503.45to5400.0 Mpa
flow	flow	mm/mm	76.2E-3-127.0E-3
density	density --		1.10to1.53
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	°C	106to202
Vicat softening temperature	Vicat softening temperature	°C	107to181
Rockwell hardness	Rockwell hardness 23℃		116to118
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃	J/m	0.028to0.055
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃	kJ/m²	1.718to2.555
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23℃	kJ/m²	6.500to11.143
Water absorption rate	Water absorption rate 23℃,24hr	%	0.70

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.