PA6 Radilon® S 32HS 100 E NAT RADIC ITALY

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	4.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	6.0 kJ/m²

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Charpy Notched Impact Strength

-30°C

ISO 179/1eA

4.5 kJ/m²

Charpy Notched Impact Strength

23°C

ISO 179/1eA

6.0 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot filament ignition temperature	Hot filament ignition temperature 2.0mm	IEC 60695-2-13	700 °C
Burning rate	Burning rate	FMVSS302	0.0 mm/min
UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	HB
Burning wire flammability index	Burning wire flammability index 1.0mm	IEC 60695-2-12	800 °C
Burning wire flammability index	Burning wire flammability index	Burning wire flammability index 2.0mm	IEC 60695-2-12	750 °C
Hot filament ignition temperature	Hot filament ignition temperature 1.0mm	IEC 60695-2-13	825 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Nominal tensile fracture strain	Nominal tensile fracture strain	ISO 527-2/1A/50	40 %
Bending modulus	Bending modulus	ISO 178	2800 MPa
bending strength	bending strength	ISO 178	105 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1A/1	3100 MPa
tensile strength	tensile strength Yield	ISO 527-2/1A/50	80.0 MPa
Tensile strain	Tensile strain Yield	ISO 527-2/1A/50	4.0 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/Bf	170 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/Af	55.0 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	195 °C
Melting temperature	Melting temperature	ISO 11357	220 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.13 g/cm³
Water absorption rate	Water absorption rate Saturation,23°C,2.00mm	ISO 62	11 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,2.00mm,50%RH	ISO 62	2.9 %
Stickiness	Stickiness H2SO4（硫酸）)	ISO 307	185 cm³/g

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	IEC 60093	1E+15 ohms·cm
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 0
Surface resistivity	Surface resistivity	IEC 60093	1E+12 ohms

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Volume resistivity

IEC 60093

1E+15 ohms·cm

Compared to the anti leakage trace index

IEC 60112

PLC 0

Surface resistivity

IEC 60093

1E+12 ohms

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.