impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C4	ISO 180/1U	140 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ASTM D4812	1700 J/m

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Suspended wall beam without notch impact strength

23°C4

ISO 180/1U

140 kJ/m²

Suspended wall beam without notch impact strength

23°C

ASTM D4812

1700 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	2410 Mpa
tensile strength	tensile strength Yield	ASTM D638	56.0 Mpa
tensile strength	tensile strength	tensile strength Break	ASTM D638	55.0 Mpa
Wear factor	Wear factor	ASTM D3702	1.0E+7 10^-8 mm³/N·m
Friction coefficient	Friction coefficient Static	ASTM D3702	0.27
Friction coefficient	Friction coefficient	Friction coefficient Dynamic	ASTM D3702	0.36
bending strength	bending strength --	ISO 178	65.0 Mpa
bending strength	bending strength	bending strength --	ASTM D790	82.0 Mpa
Bending modulus	Bending modulus --	ISO 178	2000 Mpa
Bending modulus	Bending modulus	Bending modulus --	ASTM D790	2310 Mpa
elongation	elongation Break	ISO 527-2	32 %
	elongation	elongation Break	ASTM D638	27 %
	elongation	elongation	elongation Yield	ASTM D638	14 %
tensile strength	tensile strength Break	ISO 527-2	53.0 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
Mold temperature	Mold temperature	80 to 95 °C
Back pressure	Back pressure	0.200 to 0.300 Mpa
Screw speed	Screw speed	30 to 60 rpm
Processing (melt) temperature	Processing (melt) temperature	270 to 280 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	295 to 305 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	280 to 295 °C
Temperature at the rear of the barrel	Temperature at the rear of the barrel	265 to 275 °C
Suggested maximum moisture content	Suggested maximum moisture content	0.15 to 0.25 %
drying time	drying time	4.0 hr
drying temperature	drying temperature	80 °C

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40 to 40°C	ASTM E831	1.0E-4 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ASTM E831	7.7E-5 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span4	ISO 75-2/Af	85.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	77.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate Flow : 24hr	ASTM D955	1.8 - 2.2 %
Shrinkage rate	Shrinkage rate Across FlowFlow : 24hr	ASTM D955	2.1 - 3.1 %
Water absorption rate	Water absorption rate 24 hr, 50% RH	ASTM D570	0.25 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

Flow : 24hr

ASTM D955

1.8 - 2.2 %

Shrinkage rate

Across FlowFlow : 24hr

ASTM D955

2.1 - 3.1 %

Water absorption rate

24 hr, 50% RH

ASTM D570

0.25 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.