PBT LNP™ LUBRICOMP™ WBL36L compound SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	32 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	3.2 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D4812	260 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	19 kJ/m²
Dart impact	Dart impact 23°C,EnergyatPeakLoad	ASTM D3763	3.50 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	ISO 6603-2	1.20 J

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Friction coefficient	Friction coefficient Static	ASTM D3702Modified	0.63
Wear factor	Wear factor Washer	ASTM D3702Modified	25.0 10^-10in^5-min/ft-lb-hr
tensile strength	tensile strength Yield	ASTM D638	37.2 MPa
	tensile strength	tensile strength Yield	ISO 527-2	37.0 MPa
		tensile strength	tensile strength Break	ASTM D638	36.5 MPa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2	36.0 MPa
Tensile modulus	Tensile modulus	ASTM D638	4140 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	4020 MPa
elongation	elongation Yield	ASTM D638	2.2 %
Tensile strain	Tensile strain Yield	ISO 527-2	2.4 %
elongation	elongation Break	ASTM D638	3.0 %
Tensile strain	Tensile strain Break	ISO 527-2	3.4 %
Bending modulus	Bending modulus	ASTM D790	4140 MPa
Bending modulus	Bending modulus	Bending modulus	ISO 178	3900 MPa
bending strength	bending strength	ASTM D790	68.9 MPa
bending strength	bending strength	bending strength	ISO 178	75.0 MPa
Friction coefficient	Friction coefficient Dynamic	ASTM D3702Modified	0.66

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	95.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	94.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	7.4E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	7.4E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	7E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	7.1E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	189 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	184 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.69 g/cm³
density	density	density	ISO 1183	1.69 g/cm³
Shrinkage rate	Shrinkage rate MD：24hr	ASTM D955	1.0to3.0 %
	Shrinkage rate	Shrinkage rate TD：24hr	ASTM D955	1.7to2.0 %
		Shrinkage rate	Shrinkage rate TD:24hr	ISO 294-4	1.9 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD:24hr	ISO 294-4	2.4 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.