| Volume resistivity | Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm |
| Flammability level | Flammability level 1.5mm | IEC 60695-11-10,-20 | HB |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179/1eA | 5.0 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | NoBreak |
| Ball Pressure Test | Ball Pressure Test H358/30 | ISO 2039-1 | 79.0 MPa |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/Bf | 97.0 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/Af | 70.0 °C |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B50 | 139 °C |
| Surface resistivity | Surface resistivity | IEC 60093 | >1.0E+15 ohms |
| Tensile strain | Tensile strain Yield | ISO 527-2/1A/50 | 3.0 % |
| density | density | ISO 1183/A | 1.16 g/cm³ |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 250°C/5.0kg | ISO 1133 | 18.0 cm³/10min |
| Tensile modulus | Tensile modulus | ISO 527-2/1A/1 | 3400 MPa |
| tensile strength | tensile strength Yield | ISO 527-2/1A/50 | 57.0 MPa |