mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness	ASTM D-758	68 M scale
tensile strength	tensile strength 初级Strain速率0.1cm/cm/min	ASTM D-638	490(48) kgf/cm
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap Izod研磨Notched	ASTM D-256	3.2(31.4) kgf.cm/cm(J/m)
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 落锤(15.2×15.2×0.3cm重1.4kg半径0.64cm)	ASTM D-256	95(10) kg.cm(J)
bending strength	bending strength 横跨比=16	ASTM D-790	1010(99) kgf/cm
Bending modulus	Bending modulus	ASTM D-790	27000 kgf/cm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature Unannealed,50℃/hr,5kg	ASTM D-1525	90 ℃
Hot deformation temperature	Hot deformation temperature Annealed2℃/min,18.6kgf/cm	ASTM D-648	85 ℃
Vicat softening temperature	Vicat softening temperature Unannealed,50℃/hr,1kg	ASTM D-1525	99 ℃
Temperature range for use	Temperature range for use 与残余应力大小有关		85 ℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D-792	1.17
Refractive index	Refractive index	ASTM D-542	1.49
Shrinkage rate	Shrinkage rate (冷模/冷件),48hrs	ASTM D-935	0.3-0.6 %
Transmittance rate	Transmittance rate	ASTM D-1003	92 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.