PC PANLITE® AD-5503 TEIJIN JAPAN
- Đặc tính:Trong suốtDòng chảy cao
- Lĩnh vực ứng dụng:Lớp quang học
- Giấy chứng nhận:SGS
So sánh
Xem giáBảng thông số kỹ thuật
| optical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Refractive index | Refractive index | ASTM D542/ISO 489 | 1.585 |
| Transmittance rate | Transmittance rate | ASTM D1003/ISO 13468 | 89 % |
| Refractive index | Refractive index | ASTM D542 | 1.585 |
| transmissivity | transmissivity 3000μm | ASTM D1003 | 89.0 % |
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch | ISO 179 | NoBreak |
| Basic Performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 300℃负荷1.2kg | ISO 1133 | 54 CM |
| Water absorption rate | Water absorption rate 放置在23℃水中24h | ISO 62 | 0.2 % |
| Shrinkage rate | Shrinkage rate Flow | 本公司制订的测定法 | 0.5-0.7 % |
| Refractive index | Refractive index | ASTM D542 | 1.585 |
| Transmittance rate | Transmittance rate 试样厚度3mm | ASTM D1003 | 89 % |
| Shrinkage rate | Shrinkage rate Across Flow | 本公司制订的测定法 | 0.5-0.7 % |
| density | density | ISO 1183 | 1200 kg/m |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile modulus | Tensile modulus | ASTM D638/ISO 527 | /2450 kg/cm²(MPa)[Lb/in²] |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 没Notched | ISO 179 | NB KJ/m |
| Tensile stress | Tensile stress 50mm/min | ISO 527-1 and ISO 527-2 | 63 Mpa |
| Bending modulus | Bending modulus 2mm/min | ISO 178 | 2400 Mpa |
| bending strength | bending strength 2mm/min | ISO 178 | 96 Mpa |
| Elongation at Break | Elongation at Break 50mm/min | ISO 527-1 and ISO 527-2 | >50 % |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 带Notched | ISO 179 | 3 KJ/m |
| elongation at yield | elongation at yield 50mm/min | ISO 527-1 and ISO 527-2 | 6 % |
| bending strength | bending strength | ASTM D790/ISO 178 | /96 kg/cm²(MPa)[Lb/in²] |
| Bending modulus | Bending modulus | ASTM D790/ISO 178 | /2400 kg/cm²(MPa)[Lb/in²] |
| elongation | elongation | ASTM D638/ISO 527 | /6 % |
| tensile strength | tensile strength | ASTM D638/ISO 527 | /63 kg/cm²(MPa)[Lb/in²] |
| Tensile modulus | Tensile modulus 1mm/min | ISO 527-1 and ISO 527-2 | 2450 Mpa |
| bending strength | bending strength | ISO 178 | 96.0 Mpa |
| Tensile modulus | Tensile modulus | ISO 527-2/1 | 2450 Mpa |
| tensile strength | tensile strength Yield | ISO 527-2/50 | 63.0 Mpa |
| Tensile strain | Tensile strain Yield | ISO 527-2/50 | 6.0 % |
| Tensile strain | Tensile strain Break | ISO 527-2/50 | >50 % |
| Bending modulus | Bending modulus | ISO 178 | 2400 Mpa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion Across Flow | ISO 11359-2 | 0.7 X10 |
| Vicat softening temperature | Vicat softening temperature 50℃/h 50N | ISO 308 | 143 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.7 mm/mm.℃ |
| Vicat softening temperature | Vicat softening temperature | ASTM D1525/ISO R306 | 143 ℃（℉） |
| Hot deformation temperature | Hot deformation temperature 1.80MPa | ISO 75-1 and ISO 75-2 | 124 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion Flow | ISO 11359-2 | 0.7 X10 |
| Hot deformation temperature | Hot deformation temperature 0.45MPa | ISO 75-1 and ISO 75-2 | 138 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 138 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 124 °C |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B50 | 143 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD | ISO 11359-2 | 7E-05 cm/cm/°C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Water absorption rate | Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| Shrinkage rate | Shrinkage rate | ASTM D955 | 0.5-0.7 % |
| density | density | ASTM D792/ISO 1183 | /1200 |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 300°C/1.2kg | ISO 1133 | 54.0 cm3/10min |
| Shrinkage rate | Shrinkage rate TD:4.00mm | Internal Method | 0.50-0.70 % |
| Shrinkage rate | Shrinkage rate MD:4.00mm | Internal Method | 0.50-0.70 % |
| Water absorption rate | Water absorption rate 23°C,24hr | ISO 62 | 0.20 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Dielectric constant | Dielectric constant | ASTM D150/IEC 60250 | 3.1 |
| Dielectric constant | Dielectric constant | ASTM D150/IEC 60250 | 3 |
| Surface resistivity | Surface resistivity | IEO 60250 | >1×10 Ω |
| Dielectric loss | Dielectric loss 100Hz，Tangent | IEO 60250 | 10 X10 |
| Arc resistance | Arc resistance | IEO 60112 | 250 |
| Dielectric loss | Dielectric loss 1MHz，Tangent | IEO 60250 | 90 X10 |
| Dielectric strength | Dielectric strength 短时间法 | IEO 60243-1 | 30 MV/m |
| Volume resistivity | Volume resistivity | IEO 60250 | >1×10 Ω.cm |
| Dielectric constant | Dielectric constant 1MHz | IEO 60250 | 3 |
| Dielectric constant | Dielectric constant 100Hz | IEO 60250 | 3.1 |
| Dielectric strength | Dielectric strength | IEC 60243-1 | 30 KV/mm |
| Relative permittivity | Relative permittivity 100Hz | IEC 60250 | 3.10 |
| Relative permittivity | Relative permittivity 1MHz | IEC 60250 | 3.00 |
| Dissipation factor | Dissipation factor 100Hz | IEC 60250 | 1E-03 |
| Dissipation factor | Dissipation factor 1MHz | IEC 60250 | 9E-03 |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index | IEC 60112 | PLC 2 |
| Surface resistivity | Surface resistivity | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm |