PC+PET Makroblend® UT235 M Covestro - Polycarbonates

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force 23°C	ISO 6603-2	4500 N
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy 23°C	ISO 6603-2	36.0 J
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	85 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180	85 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	85 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	85 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending strain	Bending strain 23°C	ISO 178	5.0 %
tensile strength	tensile strength Break,23°C	ISO 527-2/5	67.0 MPa
tensile strength	tensile strength	tensile strength Yield,23°C	ISO 527-2/5	68.0 MPa
Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	4500 MPa
bending strength	bending strength 3.5%Strain,23°C	ISO 178	110 MPa
bending strength	bending strength	bending strength 23°C	ISO 178	115 MPa
Bending modulus	Bending modulus 23°C	ISO 178	4650 MPa
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	4.0 %
Tensile strain	Tensile strain	Tensile strain Yield,23°C	ISO 527-2/5	3.5 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature	ISO 306/B120	139 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	114 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to85°C	ISO 11359-2	4.8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to85°C	ISO 11359-2	4.5E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	128 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate TD:270°C,3.00mm	ISO 2577	0.50to0.60 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 270°C/5.0kg	ISO 1133	39.0 cm³/10min
density	density 23°C	ISO 1183	1.34 g/cm³
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.20 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.40 %
Shrinkage rate	Shrinkage rate MD:270°C,3.00mm	ISO 2577	0.50to0.60 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.