PA6 Latamid 6 H2PX-V0 LATI S.p.A.
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | 85 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 6.0 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 1.5mm | UL 94 | V-0 |
| UL flame retardant rating | UL flame retardant rating 0.75mm | UL 94 | V-0 |
| Extreme Oxygen Index | Extreme Oxygen Index | ASTM D2863 | 28 % |
| Hot filament ignition temperature | Hot filament ignition temperature 2.0mm | IEC 60695-2-13 | 800 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 1.0mm | IEC 60695-2-13 | 800 °C |
| Burning wire flammability index | Burning wire flammability index 2.0mm | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | Burning wire flammability index 1.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | UL flame retardant rating 3.0mm | UL 94 | V-0 |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile strain | Tensile strain Yield,23°C | ISO 527-2/5 | 4.0 % |
| Tensile strain | Tensile strain Break,23°C | ISO 527-2/5 | 10 % |
| Tensile strain | Tensile strain Break,60°C | ISO 527-2/5 | 70 % |
| Tensile strain | Tensile strain Break,90°C | ISO 527-2/5 | >100 % |
| Tensile strain | Tensile strain Break,120°C | ISO 527-2/5 | >100 % |
| Tensile strain | Tensile strain Break,150°C | ISO 527-2/5 | >100 % |
| tensile strength | tensile strength Break,60°C | ISO 527-2/5 | 25.0 MPa |
| tensile strength | tensile strength Break,23°C | ISO 527-2/5 | 35.0 MPa |
| tensile strength | tensile strength Yield,23°C | ISO 527-2/5 | 40.0 MPa |
| Tensile modulus | Tensile modulus 150°C | ISO 527-2/1 | 350 MPa |
| Tensile modulus | Tensile modulus 120°C | ISO 527-2/1 | 450 MPa |
| Tensile modulus | Tensile modulus 90°C | ISO 527-2/1 | 650 MPa |
| Tensile modulus | Tensile modulus 60°C | ISO 527-2/1 | 1100 MPa |
| Tensile modulus | Tensile modulus 23°C | ISO 527-2/1 | 2700 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：30to100°C | ISO 11359-2 | 6E-05 cm/cm/°C |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B50 | 160 °C |
| Continuous use temperature | Continuous use temperature | 90.0 °C | |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 60.0 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 140 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| density | density | ISO 1183 | 1.32 g/cm³ |
| Shrinkage rate | Shrinkage rate TD:2.00mm | ISO 294-4 | 1.2to1.5 % |
| Shrinkage rate | Shrinkage rate MD:2.00mm | ISO 294-4 | 1.1to1.5 % |
| Water absorption rate | Water absorption rate 23°C,24hr | ISO 62 | 0.38 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Compared to the anti leakage trace index | Compared to the anti leakage trace index SolutionA | IEC 60112 | PLC 2 |
| Supplementary Information | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| dimensional stability | dimensional stability | 77.0 |