| Tensile modulus | Tensile modulus | ISO 527-2 | 2300 MPa |
| tensile strength | tensile strength Yield,23°C | ISO 527-2 | 53.0 MPa |
| Ball Pressure Test | Ball Pressure Test | ISO 2039-1 | 95.0 MPa |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 0.25 % |
| Water absorption rate | Water absorption rate Saturation,23°C | ISO 62 | 0.90 % |
| thermal conductivity | thermal conductivity | DIN 52612 | 0.17 W/m/K |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD | ISO 11359-2 | 7.0E-5到9.0E-5 cm/cm/°C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 120 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/A50 | 136 °C |
| Dissipation factor | Dissipation factor 1MHz | IEC 60250 | 0.015 |
| Dissipation factor | Dissipation factor 100Hz | IEC 60250 | 6E-03 |
| Dielectric constant | Dielectric constant 100Hz | IEC 60250 | 3.40 |
| Volume resistivity | Volume resistivity | IEC 60093 | 1E+14 ohms·cm |
| Surface resistivity | Surface resistivity | IEC 60093 | 1E+13 ohms |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Annealed | ISO 75-2/B | 125 °C |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/A | 60 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180/A | 15 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179 | 60 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179 | 20 kJ/m² |
| Shrinkage rate | Shrinkage rate | ISO 294-4 | 0.50to0.90 % |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 260°C/5.0kg | ISO 1133 | 14.0 cm³/10min |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 220°C/10.0kg | ISO 1133 | 3.50 cm³/10min |
| density | density | ISO 1183 | 1.15 g/cm³ |
| elongation | elongation Break | ISO 527-3 | >50 % |
| bending strength | bending strength | ISO 178 | 78.0 MPa |
| Tensile strain | Tensile strain Yield,23°C | ISO 527-2 | 4.9 % |
| Tensile creep modulus | Tensile creep modulus 1hr | ISO 899-1 | 2000 MPa |
| Tensile creep modulus | Tensile creep modulus 1000hr | ISO 899-1 | 1600 MPa |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Annealed | ISO 75-2/A | 106 °C |