flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
FMVSS combustion rate	FMVSS combustion rate	FMVSS 302	B
雾化 - G-value (condensate)	雾化 - G-value (condensate)	ISO 6452	6.0E-4 g
UL flame retardant rating	UL flame retardant rating	UL 94	HB
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating	UL 94	HB
Burning rate	Burning rate 1.00 mm	ISO 3795	28 mm/min

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	280 Mpa
Bending modulus	Bending modulus	ISO 178	9500 Mpa
Tensile strain	Tensile strain Break	ISO 527-2	3.0 %
tensile strength	tensile strength Break	ISO 527-2	200 Mpa
Tensile modulus	Tensile modulus	ISO 527-2	11000 Mpa

injection	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature		80 °C
Drying time - hot air dryer	Drying time - hot air dryer		2.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content		0.20 %
Processing (melt) temperature	Processing (melt) temperature		275 to 295 °C
Melt Temperature, Optimum	Melt Temperature, Optimum		285 °C
Mold temperature	Mold temperature		70 to 120 °C
Mold Temperature, Optimum	Mold Temperature, Optimum		100 °C
Maintain pressure	Maintain pressure		50.0 to 100 Mpa
Maintain pressure	Maintain pressure	Maintain pressure Drying Recommended		yes
Hold Pressure Time	Hold Pressure Time		3.00 s/mm
Maximum Screw Tangential Speed	Maximum Screw Tangential Speed		12 m/min

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : 55 to 160°C	ISO 11359-2	1.4E-4 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40 to 23°C	ISO 11359-2	6.5E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow	ISO 11359-2	8.3E-5 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : 55 to 160°C	ISO 11359-2	1.3E-5 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 23°C	ISO 11359-2	2.4E-5 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow	ISO 11359-2	1.8E-5 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	262 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed	ISO 75-2/A	252 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed	ISO 75-2/B	261 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.8 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation, 23°C, 2.00 mm	ISO 62	5.7 %
Shrinkage rate	Shrinkage rate Flow	ISO 294-4	0.30 %
Shrinkage rate	Shrinkage rate	Shrinkage rate 横向Flow	ISO 294-4	1.1 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 1
Compared to the anti leakage trace index	Compared to the anti leakage trace index	UL 746	PLC 1

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Compared to the anti leakage trace index

IEC 60112

PLC 1

Compared to the anti leakage trace index

UL 746

PLC 1

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.