impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.18mm	ASTM D256	160 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	3.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,6.35mm	ASTM D256	29 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.18mm	ASTM D256	29 J/m
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	13 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	2.8 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -5°C	ISO 180/1U	16 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,6.35mm	ASTM D256	150 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	800 MPa
bending strength	bending strength	bending strength	ASTM D790	78.0 MPa
Bending modulus	Bending modulus	ISO 178	77000 MPa
Bending modulus	Bending modulus	Bending modulus	ASTM D790	7600 MPa
tensile strength	tensile strength Yield	ISO 527-2/5	620 MPa
tensile strength	tensile strength	tensile strength Yield	ASTM D638	61.0 MPa
Tensile strain	Tensile strain Break	ISO 527-2/5	1.5 %
elongation	elongation Break	ASTM D638	1.5 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,4.00mm	ISO 75-2/A	250 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	250 °C

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Hot deformation temperature

1.8MPa,Unannealed,4.00mm

ISO 75-2/A

250 °C

Hot deformation temperature

1.8MPa,Unannealed,6.40mm

ASTM D648

250 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ASTM D1238	20 g/10min
density	density	ISO 1183	1.61 g/cm³
density	density	density	ASTM D792	1.61 g/cm³
ash content	ash content --	ASTM D5630	41 %
ash content	ash content	ash content --	ISO 3451	41 %
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ISO 1133	20 g/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.