MMBS ZYLAR® 670 INEOS Barex
So sánhBảng thông số kỹ thuật
| optical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Refractive index | Refractive index | ASTM D542 | 1.560 |
| Refractive index | Refractive index | ISO 489 | 1.560 |
| transmissivity | transmissivity 550nm | ASTM D1003 | 91.0 % |
| turbidity | turbidity | ASTM D1003 | 2.0 % |
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Dart impact | Dart impact | ASTM D5420 | 7.91 J |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength | ISO 180 | 140 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/A | 6.0 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ASTM D256 | 110 J/m |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179 | 130 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179 | 4.0 kJ/m² |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile modulus | Tensile modulus | ISO 527-2 | 1800 MPa |
| Tensile modulus | Tensile modulus | ASTM D638 | 1830 MPa |
| bending strength | bending strength | ISO 178 | 41.0 MPa |
| bending strength | bending strength | ASTM D790 | 41.4 MPa |
| Bending modulus | Bending modulus | ISO 178 | 1800 MPa |
| Bending modulus | Bending modulus | ASTM D790 | 1830 MPa |
| Tensile strain | Tensile strain Break,23°C | ISO 527-2 | 42 % |
| elongation | elongation Break | ASTM D638 | 42 % |
| tensile strength | tensile strength Yield,23°C | ASTM D638 | 27.6 MPa |
| tensile strength | tensile strength Yield,23°C | ISO 527-2 | 28.0 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Maximum operating temperature | Maximum operating temperature | 250 °C | |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B50 | 72.0 °C |
| Vicat softening temperature | Vicat softening temperature | ASTM D15252 | 97.8 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| density | density | ASTM D792 | 1.05 g/cm³ |
| density | density | ISO 1183 | 1.05 g/cm³ |
| Shrinkage rate | Shrinkage rate MD | ASTM D955 | 0.20to0.60 % |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 220°C/10.0kg | ISO 1133 | 55.0 cm³/10min |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 200°C/5.0kg | ISO 1133 | 6.00 cm³/10min |
| melt mass-flow rate | melt mass-flow rate 200°C/5.0kg | ASTM D1238 | 6.0 g/10min |
| Shrinkage rate | Shrinkage rate | ISO 294-4 | 0.20to0.60 % |
| Water absorption rate | Water absorption rate Saturation,23°C | ASTM D570 | 0.10 % |
| Water absorption rate | Water absorption rate Saturation,23°C | ISO 62 | 0.10 % |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 0.050 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Surface resistivity | Surface resistivity | IEC 60093 | >1.0E+14 ohms |
| Volume resistivity | Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm |
| Dielectric constant | Dielectric constant 100Hz | IEC 60250 | 2.50 |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Rockwell hardness | Rockwell hardness M-Scale | 70 | |
| Rockwell hardness | Rockwell hardness M-Scale | ASTM D785 | 70 |