mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Elongation at Break	Elongation at Break	ASTM D-638	1.2 %
tensile strength	tensile strength Break	ASTM D-638	48.0 MPa
tensile strength	tensile strength	tensile strength Yield	ASTM D-638	48.0 MPa
Tensile modulus	Tensile modulus	ASTM D-638	3130 MPa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃,3.20mm	ASTM D-256	11.0 J/m
bending strength	bending strength	ASTM D-790	69.0 MPa
Bending modulus	Bending modulus	ASTM D-790	3500 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Combustibility	Combustibility 1.47mm	UL 94	HB
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	ASTM D-696	0.000090 cm/cm℃
Vicat softening temperature	Vicat softening temperature Rate B,Loading 1(10N)	ASTM D-1525	93.0 ℃
Hot deformation temperature	Hot deformation temperature 0.45MPa，Unannealed	ASTM D-648	81.0 ℃
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.80MPa，Unannealed	ASTM D-648	73.0 ℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate Flow	ASTM D-955	0.30-0.70 %
density	density	ASTM D-792	1.04

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

Flow

ASTM D-955

0.30-0.70 %

density

ASTM D-792

1.04

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.