mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength 横夸比=16	ASTM D-790	1460(143) Kgf/cm
Bending modulus	Bending modulus	ASTM D-790	34000 Kgf/cm
tensile strength	tensile strength 初级Strain速率0.1cm/cm/min	ASTM D-638	767(75) Kgf/cm
Rockwell hardness	Rockwell hardness	ASTM D-758(M级)	99
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 落锤(15.215.20.3cm)重1.4kg 半径0.64cm	ASTM D-256	14(1.6) kg-cm(J)
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap Lzod 研磨Notched	ASTM D-256	1.5(14.7) kgf-cm/cm(J/m)

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature 50℃/hr,1kg	ASTM D-1525	235 F
Temperature range for use	Temperature range for use 与残余应力大小有关		85-105
Vicat softening temperature	Vicat softening temperature Unannealed	ASTM D-1525	113 °C
Hot deformation temperature	Hot deformation temperature HDT	ASTM D-648	103 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate	ASTM D-955	0.4-0.8 %
density	density	ASTM D-792	1.18
Flame retardant performance	Flame retardant performance	UL 94	HB CLASS
Refractive index	Refractive index	ASTM D-542	1.49
Transmittance rate	Transmittance rate	ASTM D-1003	93 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.