PBT VALOX™ 364 resin SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ASTM D256	430 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C	ASTM D256	690 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	750 J/m
Dart impact	Dart impact -40°C,TotalEnergy	ASTM D3763	47.5 J
	Dart impact	Dart impact -20°C,TotalEnergy	ASTM D3763	44.7 J
	Dart impact	Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	45.2 J

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	5VA
Extreme Oxygen Index	Extreme Oxygen Index	ASTM D2863	28 %

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.5mm

UL 94

V-0

UL flame retardant rating

3.0mm

UL 94

5VA

Extreme Oxygen Index

ASTM D2863

28 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield	ASTM D638	46.9 MPa
tensile strength	tensile strength	tensile strength Break	ASTM D638	40.0 MPa
elongation	elongation Yield	ASTM D638	5.0 %
elongation	elongation	elongation Break	ASTM D638	70 %
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	1860 MPa
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	66.9 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	103 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	68.3 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15254	115 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature	ISO 306/B120	122 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	9.5E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	9.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	9.8E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	1E-04 cm/cm/°C
RTI Elec	RTI Elec	UL 746	75.0 °C
RTI Imp	RTI Imp	UL 746	75.0 °C
RTI Str	RTI Str	UL 746	75.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.30 g/cm³
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.80to1.0 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD：3.20mm	Internal Method	0.80to1.0 %
Outdoor applicability	Outdoor applicability	UL 746C	f2

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 0
High arc combustion index	High arc combustion index HAI	UL 746	PLC 0
High voltage arc tracing rate	High voltage arc tracing rate HVTR	UL 746	PLC 2
Hot wire ignition	Hot wire ignition HWI	UL 746	PLC 2
Arc resistance	Arc resistance	ASTM D495	PLC 5

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.