ABS+PBT EXCELLOY TK10 Techno Polymer Co, Ltd.

So sánh

Bảng thông số kỹ thuật

	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	83.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	99.0 °C
density	density	ISO 1183	1.08 g/cm³
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ASTM D256	290 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	ISO 179	28 kJ/m²
bending strength	bending strength --	ISO 178	60.0 MPa
bending strength	bending strength	bending strength --	ASTM D790	69.6 MPa
Bending modulus	Bending modulus --	ISO 178	1870 MPa
Bending modulus	Bending modulus	Bending modulus --	ASTM D790	2260 MPa
tensile strength	tensile strength Yield	ISO 527-2	40.0 MPa
tensile strength	tensile strength	tensile strength Yield	ASTM D638	41.2 MPa
Rockwell hardness	Rockwell hardness R-Sale	ISO 2039-2	104
Rockwell hardness	Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	105
Shrinkage rate	Shrinkage rate	ISO 294-4	0.40to0.70 %
melt mass-flow rate	melt mass-flow rate 240°C/10.0kg	ISO 1133	12 g/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.