| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Multi axis Instrumented Peak Impact Force | Multi axis Instrumented Peak Impact Force 23°C | ISO 6603-2 | 1000 N |
| Multi axis Instrumented Peak Impact Force | Multi axis Instrumented Peak Impact Force -30°C | ISO 6603-2 | 650 N |
| Multi axis Instrumented Impact Energy | Multi axis Instrumented Impact Energy 23°C | ISO 6603-2 | 13.0 J |
| Multi axis Instrumented Impact Energy | Multi axis Instrumented Impact Energy -30°C | ISO 6603-2 | 4.80 J |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | 70 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | 80 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 1.6mm | UL 94 | HB |
| UL flame retardant rating | UL flame retardant rating 3.2mm | UL 94 | HB |
| Burning wire flammability index | Burning wire flammability index 2.0mm | IEC 60695-2-12 | 650 °C |
| Extreme Oxygen Index | Extreme Oxygen Index | ISO 4589-2 | 22 % |
| BurningBehavior | BurningBehavior | ISO 3795 | passed |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Bending strain | Bending strain 23°C | ISO 178/A | 5.0 % |
| bending strength | bending strength 23°C4 | ISO 178/A | 130 Mpa |
| bending strength | bending strength 3.5%Strain,23°C | ISO 178/A | 125 Mpa |
| Bending modulus | Bending modulus 23°C | ISO 178/A | 4000 Mpa |
| Tensile strain | Tensile strain Break,23°C | ISO 527-2/5 | 4.5 % |
| tensile strength | tensile strength Break,23°C | ISO 527-2/5 | 85.0 Mpa |
| Tensile modulus | Tensile modulus 23°C | ISO 527-2/1 | 4500 Mpa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 205 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：23to55°C | ISO 11359-2 | 1.5E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：23to55°C | ISO 11359-2 | 4E-05 cm/cm/°C |
| Melting temperature | Melting temperature | ISO 11357-3 | 214 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B120 | 200 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 200 °C |
| Hot deformation temperature | Hot deformation temperature 8.0MPa,Unannealed | ISO 75-2/C | 60.0 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 175 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Apparent density | Apparent density | ISO 60 | 0.60 g/cm³ |
| Shrinkage rate | Shrinkage rate TD:280°C,2.00mm2 | ISO 2577 | 0.61 % |
| Shrinkage rate | Shrinkage rate TD:120°C,4hr,2.00mm3 | ISO 2577 | 0.15 % |
| Shrinkage rate | Shrinkage rate MD:280°C,2.00mm2 | ISO 2577 | 0.59 % |
| Shrinkage rate | Shrinkage rate MD:120°C,4hr,2.00mm3 | ISO 2577 | 0.14 % |
| Water absorption rate | Water absorption rate Saturation,23°C | ISO 62 | 7.0 % |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 2.0 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Relative permittivity | Relative permittivity 23°C,100Hz | IEC 60250 | 3.50 |
| Dielectric strength | Dielectric strength 23°C,1.00mm | IEC 60243-1 | 43 KV/mm |
| Volume resistivity | Volume resistivity 23°C | IEC 60093 | 1E+13 ohms·cm |
| Surface resistivity | Surface resistivity | IEC 60093 | 1E+15 ohms |
| Relative permittivity | Relative permittivity 23°C,1MHz | IEC 60250 | 3.20 |
| Dissipation factor | Dissipation factor 23°C,100Hz | IEC 60250 | 6E-03 |
| Dissipation factor | Dissipation factor 23°C,1MHz | IEC 60250 | 0.015 |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index SolutionA | IEC 60112 | PLC 0 |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Ball Pressure Test | Ball Pressure Test | ISO 2039-1 | 110 Mpa |
| Supplementary Information | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| ISO Shortcut | ISO Shortcut | ISO 1874 | PA6/66HI.GR.14-040.GF15 |