impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -20°C	ASTM D256	8.4 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180	12 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -20°C,4.00mm	ASTM D256	NoBreak
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C,4.00mm	ASTM D256	NoBreak
		Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -20°C	ISO 180	NoBreak
		Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ASTM D256	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C,4.00mm，Area	ASTM D256	4.20 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,4.00mm，Area	ASTM D256	12.6 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C	ISO 180	4.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength -20°C	ISO 179	10 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	15 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ASTM D256	15 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -20°C	ASTM D256	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -20°C	ISO 179	NoBreak

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus 4.00mm	ISO 178	1000 MPa
tensile strength	tensile strength Yield	ASTM D638	23.0 MPa
	tensile strength	tensile strength Yield	ISO 527-2	23.0 MPa
	tensile strength	tensile strength	tensile strength 4.00mm	ISO 527-2	12.0 MPa
elongation	elongation Yield	ASTM D638	15 %
Tensile strain	Tensile strain Yield	ISO 527-2	15 %
elongation	elongation Break	ASTM D638	300 %
Tensile strain	Tensile strain Break,4.00mm	ISO 527-2	300 %
Bending modulus	Bending modulus 4.00mm	ASTM D790	1000 MPa
tensile strength	tensile strength	ASTM D638	12.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/Bf	76.0 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648A	45.0 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/Af	45.0 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	125 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	63.0 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648B	76.1 °C
Vicat softening temperature	Vicat softening temperature --	ASTM D15253	125 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ASTM D15254	62.8 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	0.996 g/cm³
density	density	density	ISO 1183	1.01 g/cm³
melt mass-flow rate	melt mass-flow rate 190°C/10.0kg	ASTM D1238	20 g/10min
	melt mass-flow rate	melt mass-flow rate 190°C/2.16kg	ASTM D1238	2.0 g/10min
		melt mass-flow rate	melt mass-flow rate 190°C/21.6kg	ASTM D1238	80 g/10min
			melt mass-flow rate	melt mass-flow rate 190°C/10.0kg	ISO 1133	20 g/10min
				melt mass-flow rate	melt mass-flow rate 190°C/2.16kg	ISO 1133	2.0 g/10min
				melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 190°C/21.6kg	ISO 1133	80 g/10min
Shrinkage rate	Shrinkage rate MD	ASTM D955	1.5to2.5 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	1.5to2.5 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	ESDSTM11.11	<1.0E+5 ohms
Surface resistivity	Surface resistivity	IEC 61340-2-3	<1.0E+5 ohms
Volume resistivity	Volume resistivity	Internal Method	<1.0E+4 ohms·cm

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Surface resistivity

ESDSTM11.11

<1.0E+5 ohms

Surface resistivity

IEC 61340-2-3

<1.0E+5 ohms

Volume resistivity

Internal Method

<1.0E+4 ohms·cm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreA	ASTM D2240	95
	Shore hardness	Shore hardness ShoreD	ASTM D2240	66
		Shore hardness	Shore hardness ShoreA	ISO 868	95
		Shore hardness	Shore hardness	Shore hardness ShoreD	ISO 868	66

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.