PC 302-7 Trinseo

So sánh

Bảng thông số kỹ thuật

optical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
turbidity	turbidity	ASTM D1003	1.0 %
transmissivity	transmissivity	ASTM D1003	86.0to90.0 %
Refractive index	Refractive index	ISO 489	1.586
Refractive index	Refractive index	Refractive index	ASTM D542	1.586

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	910 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	370 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	80 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	32 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

3.0mm

UL 94

UL flame retardant rating

1.5mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	2280 MPa
bending strength	bending strength	ISO 178	92.0 MPa
elongation	elongation Break	ASTM D638	170 %
Tensile strain	Tensile strain Yield	ISO 527-2/50	6.0 %
elongation	elongation Yield	ASTM D638	6.0 %
tensile strength	tensile strength Break	ISO 527-2/50	72.0 MPa
	tensile strength	tensile strength Break	ASTM D638	71.7 MPa
		tensile strength	tensile strength Yield	ISO 527-2/50	61.0 MPa
		tensile strength	tensile strength	tensile strength Yield	ASTM D638	60.7 MPa
Tensile modulus	Tensile modulus	ISO 527-2/50	2300 MPa
Taber wear resistance	Taber wear resistance	ASTM D1044	20 %
Tensile strain	Tensile strain Break	ISO 527-2/50	170 %
Bending modulus	Bending modulus	ASTM D790	2280 MPa
Bending modulus	Bending modulus	Bending modulus	ISO 178	2300 MPa
bending strength	bending strength	ASTM D790	93.8 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature --	ASTM D15257	153 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/A120	153 °C
		Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	147 °C
		Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ASTM D15256	147 °C
Glass transition temperature	Glass transition temperature	ASTM D3418	149 °C
Glass transition temperature	Glass transition temperature	Glass transition temperature	ISO 11357-2	149 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to82°C	ASTM D696	6.8E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.32 %
density	density	ASTM D792	1.20 g/cm³
density	density	density	ISO 1183/B	1.20 g/cm³
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ASTM D1238	7.0 g/10min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ISO 1133	7.0 g/10min
Shrinkage rate	Shrinkage rate MD	ASTM D955	0.50to0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.50to0.70 %
Water absorption rate	Water absorption rate 23°C,24hr	ASTM D570	0.15 %
	Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.15 %
	Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ASTM D570	0.32 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.