mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength	ISO 527-2	29 MPa
elongation	elongation	ISO 527-2	4 %
Bending modulus	Bending modulus	MPa	IS0 180 3200
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20℃	ISO 180	3 kj/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 0℃	ISO 180	3 kj/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃	ISO 180	4 kj/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 0℃	ISO 180	16 kj/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23℃	ISO 180	26 kj/m

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa	ISO 75-2/B	116 ℃
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.80MPa	ISO 75-2/A	66 ℃
Vicat softening temperature	Vicat softening temperature	ISO 306/A50	154 ℃
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature	ISO 306/B50	96 ℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate	ISO 294-4	0.60-0.70 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

ISO 294-4

0.60-0.70 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.