impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -40°C,Injection	ISO 179/1eU	50 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C,Injection	ISO 180/4A	6.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 0°C,Injection	ISO 180/4A	10 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,Injection	ISO 180/4A	30 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -40°C,Injection	ISO 179/1eU	50 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C,Injection	ISO 180/4A	6.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 0°C,Injection	ISO 180/4A	10 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,Injection	ISO 180/4A	30 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus Injection	ASTM D790	1550 MPa
tensile strength	tensile strength Yield,Injection	ISO 527-2/1A/50	22.0 MPa
tensile strength	tensile strength	tensile strength Break,Injection	ISO 527-2/1A/50	18.0 MPa
Tensile strain	Tensile strain Break,Injection	ISO 527-2/1A/50	100 %
Bending modulus	Bending modulus Injection	ASTM D790	1550 MPa
tensile strength	tensile strength Yield,Injection	ISO 527-2/1A/50	22.0 MPa
tensile strength	tensile strength	tensile strength Break,Injection	ISO 527-2/1A/50	18.0 MPa
Tensile strain	Tensile strain Break,Injection	ISO 527-2/1A/50	100 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	105 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-30to30°C	ASTM D696	6.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to80°C	ASTM D696	1E-04 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	105 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-30to30°C	ASTM D696	6.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to80°C	ASTM D696	1E-04 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	0.960 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	23 g/10min
Shrinkage rate	Shrinkage rate 24hr	Internal Method	0.90 %
density	density	ISO 1183	0.960 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	23 g/10min
Shrinkage rate	Shrinkage rate 24hr	Internal Method	0.90 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreD,Injection	ISO 868	64
Shore hardness	Shore hardness ShoreD,Injection	ISO 868	64

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shore hardness

ShoreD,Injection

ISO 868

Shore hardness

ShoreD,Injection

ISO 868

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.