PP Homopolymer WPP PP PPH2GF3-Black Washington Penn Plastic Co. Inc.

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	35 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180	9.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ISO 180	6.5 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	95 J/m
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	43 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	9.5 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	600 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	118 MPa
Bending modulus	Bending modulus	ISO 178	5400 MPa
Bending modulus	Bending modulus	Bending modulus	ASTM D790	5100 MPa
Tensile strain	Tensile strain Break	ISO 527-2/50	6.5 %
Tensile strain	Tensile strain	Tensile strain Yield	ISO 527-2/50	6.5 %
tensile strength	tensile strength Break	ISO 527-2/50	88.0 MPa
	tensile strength	tensile strength Break	ISO 527-2	78.0 MPa
		tensile strength	tensile strength Break	ASTM D638	78.0 MPa
		tensile strength	tensile strength	tensile strength Yield	ISO 527-2/50	75.0 MPa
UltimateTensileStrength	UltimateTensileStrength	ISO 527	80.0 MPa
elongation	elongation Break	ASTM D638	6.0 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	146 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	148 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	156 °C
Vicat softening temperature	Vicat softening temperature	ASTM D1525	161 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/Af	141 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.12 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ASTM D1238	4.5 g/10min
density	density	ASTM D792	1.12 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	4.5 g/10min

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreD	ASTM D2240	75

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shore hardness

ShoreD

ASTM D2240

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.