| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | kJ/m² | 7.5 8.5 |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | | 无断裂 -- |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | °C | 105 -- |
| Vicat softening temperature | Vicat softening temperature | °C | 123 -- |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：23to55°C | cm/cm/°C | 1.1E-04 -- |
| density | density 23°C | g/cm³ | 1.16 -- |
| melt mass-flow rate | melt mass-flow rate 260°C/5.0kg | g/10min | 32 -- |
| Shrinkage rate | Shrinkage rate 23°C | % | 0.50to0.80 -- |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | kJ/m² | 5.0 -- |
| bending strength | bending strength 23°C | MPa | 76.0 57.0 |
| Bending modulus | Bending modulus 23°C | MPa | 2400 1500 |
| Tensile strain | Tensile strain Break,50°C | % | >30 -- |
| tensile strength | tensile strength 23°C | MPa | 52.0 37.0 |
| Tensile modulus | Tensile modulus 23°C | MPa | 2950 1700 |
| Water absorption rate | Water absorption rate 23°C,24hr | % | 1.0 -- |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | | 无断裂 |