PPO(PPE)+PS+PA NORYL GTX™ GTX987 resin SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	10.0 J
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C8	ISO 180/1A	15 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C8	ISO 180/1A	8.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	90 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	70 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	11 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation Break	ISO 527-2/50	20 %
Bending modulus	Bending modulus 50.0mmSpan4	ASTM D790	2700 MPa
Bending modulus	Bending modulus	Bending modulus --5	ISO 178	2800 MPa
Tensile modulus	Tensile modulus --2	ASTM D638	3250 MPa
elongation	elongation Break3	ASTM D638	15 %
	elongation	elongation Yield	ISO 527-2/50	5.0 %
	elongation	elongation	elongation Yield3	ASTM D638	5.0 %
tensile strength	tensile strength Break	ISO 527-2/50	62.0 MPa
	tensile strength	tensile strength Break3	ASTM D638	55.0 MPa
		tensile strength	tensile strength Yield	ISO 527-2/50	62.0 MPa
		tensile strength	tensile strength	tensile strength Yield3	ASTM D638	55.0 MPa
Tensile modulus	Tensile modulus --	ISO 527-2/1	3000 MPa
bending strength	bending strength Yield,50.0mmSpan4	ASTM D790	95.0 MPa
bending strength	bending strength	bending strength --5,6	ISO 178	90.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	198 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	200 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:-40to60°C	ASTME831	5.5E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature --	ASTM D152510	192 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan9	ISO 75-2/Bf	190 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	185 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:23to60°C	ISO 11359-2	7.5E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:-40to60°C	ASTME831	6E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:23to60°C	ISO 11359-2	7E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.90 %
density	density	ASTMD792	1.25 g/cm³
melt mass-flow rate	melt mass-flow rate 280°C/5.0kg	ASTM D1238	8.5 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 280°C/5.0kg	ISO 1133	7.50 cm³/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	1.0to1.4 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	3.0 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.