PP SABIC® PP 48M10 SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -20°C	ISO 179/1eA	6.0 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength 0°C	ISO 179/1eA	7.0 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	11 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C	ASTM D256A	65 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 0°C	ASTM D256A	75 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256A	90 J/m
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C	ISO 180/1A	5.0 kJ/m²
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 0°C	ISO 180/1A	7.0 kJ/m²
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	8.0 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus 1%Secant3	ASTM D638	1500 MPa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1A/1	1400 MPa
tensile strength	tensile strength Yield4	ASTM D638	26.0 MPa
tensile strength	tensile strength	tensile strength Yield	ISO 527-2/1A/50	26.0 MPa
elongation	elongation Yield4	ASTM D638	5.0 %
elongation	elongation	elongation Yield	ISO 527-2/1A/50	5.0 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature --	ASTMD15256	151 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ASTMD15257	79.0 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	95.0 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed5	ISO 75-2/Bf	90.0 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	60.0 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed5	ISO 75-2/Af	55.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ASTMD1238	15 g/10min
density	density	ASTMD792	0.905 g/cm³

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

melt mass-flow rate

230°C/2.16kg

ASTMD1238

15 g/10min

density

ASTMD792

0.905 g/cm³

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	95
Shore hardness	Shore hardness ShoreD	ISO 868	65

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

Shore hardness

ShoreD

ISO 868

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.