PC LEXAN™ EXL9330 BK1A068 SABIC INNOVATIVE NANSHA

Đặc tính:
Chống tia cực tím
Tăng cường
Chống cháy
Lĩnh vực ứng dụng:
Thực phẩm
Sản phẩm tường mỏng
Trang chủ
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	60 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	75 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C, 6.40 mm	ASTM D256	640 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C9	ISO 180/1A	55 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C10	ISO 180/4A	65 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C9	ISO 180/1A	70 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -50°C	ASTM D256	590 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	680 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	800 J/m
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C8	Internal Method	1100 J/m
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C10	ISO 180/4A	80 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	无断裂
Dart impact	Dart impact 23°C, Total Energy	ASTM D3763	52.0 J

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.0 mm	UL 94	5VA
Burning wire flammability index	Burning wire flammability index 1.0 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature 1.0 mm	IEC 60695-2-13	825 °C
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	35 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength Yield, 50.0 mm Span4	ASTM D790	88.0 Mpa
bending strength	bending strength	bending strength --5,6	ISO 178	85.0 Mpa
Bending modulus	Bending modulus --5	ISO 178	2200 Mpa
Bending modulus	Bending modulus	Bending modulus 50.0 mm Span4	ASTM D790	2060 Mpa
elongation	elongation Break	ISO 527-2/50	130 %
	elongation	elongation Break3	ASTM D638	130 %
		elongation	elongation Yield	ISO 527-2/50	6.0 %
		elongation	elongation	elongation Yield3	ASTM D638	6.0 %
tensile strength	tensile strength Break	ISO 527-2/50	60.0 Mpa
	tensile strength	tensile strength Break3	ASTM D638	61.0 Mpa
		tensile strength	tensile strength Yield	ISO 527-2/50	55.0 Mpa
		tensile strength	tensile strength	tensile strength Yield3	ASTM D638	58.0 Mpa
Tensile modulus	Tensile modulus --	ISO 527-2/1	2100 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --2	ASTM D638	2100 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
Spray nozzle temperature	Spray nozzle temperature	290 to 310 °C
Processing (melt) temperature	Processing (melt) temperature	295 to 315 °C
Mold temperature	Mold temperature	70 to 95 °C
Back pressure	Back pressure	0.300 to 0.700 Mpa
Screw speed	Screw speed	40 to 70 rpm
Exhaust hole depth	Exhaust hole depth	0.025 to 0.076 mm
drying temperature	drying temperature	120 °C
drying time	drying time	3.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
Suggested injection volume	Suggested injection volume	40 to 60 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	215 to 295 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	280 to 305 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	295 to 315 °C

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 3.20 mm	ASTM D648	134 °C
	Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span11	ISO 75-2/Be	135 °C
		Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	120 °C
			Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm	ASTM D648	124 °C
			Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span11	ISO 75-2/Ae	124 °C
Vicat softening temperature	Vicat softening temperature --	ASTM D152512	142 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	140 °C
Ball Pressure Test	Ball Pressure Test 123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ASTM E831	6.7E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : 23 to 80°C	ISO 11359-2	7.2E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40 to 40°C	ASTM E831	6.7E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : 23 to 80°C	ISO 11359-2	7.7E-5 cm/cm/°C
RTI Elec	RTI Elec	UL 746	125 °C
RTI Imp	RTI Imp	UL 746	115 °C
RTI	RTI	UL 746	120 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Outdoor applicability	Outdoor applicability	UL 746C	f1
Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	0.15 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation, 23°C	ISO 62	0.35 %
Shrinkage rate	Shrinkage rate Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.80 %
Shrinkage rate	Shrinkage rate	Shrinkage rate Flow : 3.20 mm	Internal Method	0.40 - 0.80 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/1.2 kg	ISO 1133	9.00 cm3/10min
melt mass-flow rate	melt mass-flow rate 300°C/1.2 kg	ASTM D1238	10 g/10 min
density	density --	ISO 1183	1.19 g/cm³
density	density	density --	ASTM D792	1.18 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 60093	> 1.0E+15 ohms
Volume resistivity	Volume resistivity	IEC 60093	> 1.0E+15 ohms·cm
Dielectric strength	Dielectric strength 3.20 mm, in Oil	ASTM D149	17 KV/mm
Dielectric strength	Dielectric strength	Dielectric strength 3.20 mm, in Oil	IEC 60243-1	16 KV/mm
Dielectric constant	Dielectric constant 60 Hz	ASTM D150	2.95
	Dielectric constant	Dielectric constant 50 kHz	ASTM D150	2.95
		Dielectric constant	Dielectric constant 1 MHz	ASTM D150	2.90
			Dielectric constant	Dielectric constant 50 Hz	IEC 60250	2.60
				Dielectric constant	Dielectric constant 60 Hz	IEC 60250	2.60
				Dielectric constant	Dielectric constant	Dielectric constant 1 MHz	IEC 60250	2.70
Dissipation factor	Dissipation factor 50 Hz	ASTM D150	2.4E-3
	Dissipation factor	Dissipation factor 60 Hz	ASTM D150	2.4E-3
		Dissipation factor	Dissipation factor 1 MHz	ASTM D150	8.5E-3
			Dissipation factor	Dissipation factor 50 Hz	IEC 60250	1.0E-3
			Dissipation factor	Dissipation factor	Dissipation factor 60 Hz	IEC 60250	1.0E-3
Compared to the anti leakage trace index	Compared to the anti leakage trace index	UL 746	PLC 3
Compared to the anti leakage trace index	Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 3
High arc combustion index	High arc combustion index	UL 746	PLC 0
Hot wire ignition	Hot wire ignition	UL 746	PLC 1

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test H 358/30	ISO 2039-1	90.0 Mpa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

H 358/30

ISO 2039-1

90.0 Mpa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.

Có thể bạn cũng quan tâm

PC EXL9330 BK1A068 Nhựa đổi mới cơ sở (Nam Sa)

₫175.860/KG