impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	60 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	55 kJ/m²

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Impact strength of simply supported beam without notch

23°C

ISO 179/1eU

60 kJ/m²

Suspended wall beam without notch impact strength

23°C

ISO 180/1U

55 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Burning wire flammability index	Burning wire flammability index 3.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature 1.5mm	IEC 60695-2-13	775 °C
Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 3.0mm	IEC 60695-2-13	775 °C
UL flame retardant rating	UL flame retardant rating 0.75mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	V-0
Burning wire flammability index	Burning wire flammability index 0.75mm	IEC 60695-2-12	960 °C
Burning wire flammability index	Burning wire flammability index	Burning wire flammability index 1.5mm	IEC 60695-2-12	960 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus 23°C	ISO 178/A	9200 Mpa
bending strength	bending strength 3.5%Strain,23°C	ISO 178/A	-- Mpa
bending strength	bending strength	bending strength 23°C4	ISO 178/A	210 Mpa
Bending strain	Bending strain 23°C	ISO 178/A	3.3 %
Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	9500 Mpa
tensile strength	tensile strength Break,23°C	ISO 527-2/5	130 Mpa
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	2.8 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melting temperature	Melting temperature	ISO 11357-3	222 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	202 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B120	213 °C
Ball Pressure Test	Ball Pressure Test 210°C	IEC 60695-10-2	Pass

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate TD:260°C,2.00mm2	ISO 2577	0.60 %
	Shrinkage rate	Shrinkage rate TD:120°C,4hr,2.00mm3	ISO 2577	0.10 %
		Shrinkage rate	Shrinkage rate MD:260°C,2.00mm2	ISO 2577	0.30 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD:120°C,4hr,2.00mm3	ISO 2577	0.10 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	5.0 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	1.5 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 60093	4E+15 ohms
Volume resistivity	Volume resistivity 23°C	IEC 60093	5E+15 ohms·cm
Dielectric strength	Dielectric strength 23°C,1.00mm	IEC 60243-1	39 KV/mm
Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 0

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ISO Shortcut	ISO Shortcut	ISO 1874	PA6.GFHR.10-090.GF25

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

ISO Shortcut

ISO 1874

PA6.GFHR.10-090.GF25

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.