Polyester, TS Synres-Almoco AMC 2567 Synres-Almoco BV

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength Compression Molded	ISO 179/1eA	2.5to3.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength Injection	ISO 179/1eA	3.5to5.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch Compression Molded	ISO 179/1eU	5.0to10 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch Injection	ISO 179/1eU	9.0to14 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot filament ignition temperature	Hot filament ignition temperature	IEC 60695-2-13	930 °C
Burning wire flammability index	Burning wire flammability index	IEC 60695-2-12	960 °C
UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 0.60mm	UL 94	V-1

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus Compression Molded	ISO 178	8000to12000 MPa
tensile strength	tensile strength Injection	ISO 527-2	60.0to70.0 MPa
tensile strength	tensile strength	tensile strength CompressionMolded	ISO 527-2	35.0to60.0 MPa
Tensile modulus	Tensile modulus Injection	ISO 527-2	13000to15000 MPa
Tensile modulus	Tensile modulus	Tensile modulus Compression Molded	ISO 527-2	6000to9000 MPa
Bending modulus	Bending modulus Injection	ISO 178	8000to12000 MPa
bending strength	bending strength Compression Molded	ISO 178	80.0to100 MPa
bending strength	bending strength	bending strength Injection	ISO 178	120to140 MPa
Compressive stress	Compressive stress	ISO 604	120to170 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
thermal conductivity	thermal conductivity	ASTME1461	0.90to1.1 W/m/K
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：50to100°C	ISO 11359-2	1.0E-5到2.0E-5 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	>200 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 8.0MPa,Unannealed	ISO 75-2/C	100to120 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate	ISO 2577	<0.050 %
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	<0.30 %
Shrinkage rate	Shrinkage rate MD3	ISO 2577	0.15to0.45 %
Apparent density	Apparent density	ISO 60	0.70to0.85 g/cm³
density	density	ISO 1183	2.00to2.20 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 0
Arc resistance	Arc resistance	ASTM D495	PLC 4
Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.010to0.030
Dissipation factor	Dissipation factor	Dissipation factor 100Hz	IEC 60250	0.010to0.030
Relative permittivity	Relative permittivity 1MHz	IEC 60250	4.005.00
Relative permittivity	Relative permittivity	Relative permittivity 100Hz	IEC 60250	5.006.00
Dielectric strength	Dielectric strength	IEC 60243-1	25to35 kV/mm
Volume resistivity	Volume resistivity	IEC 60093	1.0E+14到1.0E+15 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	1.0E+13到1.0E+14 ohms

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.