mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation Break,23°C	ASTM D638	300 %
Bending modulus	Bending modulus 23°C	ASTM D790	150 MPa
Friction coefficient	Friction coefficient	ASTM D1894	>1.0
Tensile modulus	Tensile modulus 23°C	ASTM D638	170 MPa
tensile strength	tensile strength Yield,23°C,3.00mm,Injection3	ASTM D638	14.0 MPa
tensile strength	tensile strength	tensile strength Break,23°C,2.00mm4	ASTM D638	20.0 MPa
elongation	elongation Yield,23°C	ASTM D638	30 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
specific heat	specific heat 150°C7	DSC	2000 J/kg/°C
	specific heat	specific heat 175°C7	DSC	2300 J/kg/°C
	specific heat	specific heat	specific heat 200°C8	DSC	3100 J/kg/°C
Glass transition temperature	Glass transition temperature	DSC	-3.00 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15256	170 °C
Brittle temperature	Brittle temperature	ASTM D746	<-75.0 °C
specific heat	specific heat 225°C9	DSC	2300 J/kg/°C
thermal conductivity	thermal conductivity 23°C	ASTMC177	0.19 W/m/K
Fusion temperature	Fusion temperature 23°C	ASTME793	27.0 kJ/kg
Melting temperature	Melting temperature	ASTM D3418	207 °C
Crystallization peak temperature	Crystallization peak temperature DSC	DSC	140 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23°C	ASTM D696	1.5E-04 cm/cm/°C
specific heat	specific heat 25°C7	DSC	1600 J/kg/°C
specific heat	specific heat	specific heat 100°C7	DSC	1800 J/kg/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.13 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ASTM D1238	20 g/10min
Water absorption rate	Water absorption rate 23°C,24hr	ASTM D570	0.35 %
Intrinsic viscosity	Intrinsic viscosity 23°C	Internal Method	1.1

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreA,23°C	ASTM D2240	95
Shore hardness	Shore hardness ShoreD,23°C	ASTM D2240	55

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shore hardness

ShoreA,23°C

ASTM D2240

Shore hardness

ShoreD,23°C

ASTM D2240

film	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation MD:Yield,130μm	ASTM D882	26 %
	elongation	elongation TD:Yield,130μm	ASTM D882	26 %
		elongation	elongation MD:Break,130μm	ASTM D882	550 %
		elongation	elongation	elongation TD:Break,130μm	ASTM D882	550 %
Oxygen permeability	Oxygen permeability 30°C,130μm	ASTM D1434	841 cm³/m²/24hr
Water vapor permeability	Water vapor permeability	ASTMF372	130 g/m²/24hr
film thickness	film thickness		130 µm
Secant modulus	Secant modulus Tangent,MD:130μm	ASTM D882	185 MPa
Secant modulus	Secant modulus	Secant modulus Tangent,TD:130μm	ASTM D882	179 MPa
tensile strength	tensile strength MD:Yield,130μm	ASTM D882	13.7 MPa
	tensile strength	tensile strength TD:Yield,130μm	ASTM D882	13.5 MPa
		tensile strength	tensile strength MD:Break,130μm	ASTM D882	23.7 MPa
		tensile strength	tensile strength	tensile strength TD:Break,130μm	ASTM D882	22.6 MPa

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tear strength	tear strength 23°C	ASTM D1004	370 N

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

tear strength

23°C

ASTM D1004

370 N

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.