PA6 Durethan® DP BKV 60 H2.0 EF 900116 LANXESS GERMANY

Đặc tính:
Đóng gói: Gia cố sợi thủy
60% đóng gói theo trọng l
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy -30°C	ISO 6603-2	3.80 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy 23°C	ISO 6603-2	4.30 J
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force -30°C	ISO 6603-2	1350 N
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	90 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	95 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	95 kJ/m²
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force 23°C	ISO 6603-2	1480 N

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending strain	Bending strain 23°C	ISO 178/A	3.0 %
bending strength	bending strength 23°C4	ISO 178/A	390 Mpa
bending strength	bending strength	bending strength 3.5%Strain,23°C	ISO 178/A	-- Mpa
Bending modulus	Bending modulus 23°C	ISO 178/A	20000 Mpa
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	2.5 %
tensile strength	tensile strength Break,23°C	ISO 527-2/5	230 Mpa
Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	19400 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to55°C	ISO 11359-2	8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	ISO 11359-2	1E-05 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	221 °C
Hot deformation temperature	Hot deformation temperature 8.0MPa,Unannealed	ISO 75-2/C	186 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	213 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	220 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	1.2 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	3.8 %
Shrinkage rate	Shrinkage rate MD:120°C,4hr,2.00mm3	ISO 2577	0.030 %
	Shrinkage rate	Shrinkage rate MD:280°C,2.00mm2	ISO 2577	0.30 %
		Shrinkage rate	Shrinkage rate TD:120°C,4hr,2.00mm3	ISO 2577	0.020 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate TD:280°C,2.00mm2	ISO 2577	0.60 %

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ISO Shortcut	ISO Shortcut	ISO 1874	PA6.GHR.10-190.GF60

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

ISO Shortcut

ISO 1874

PA6.GHR.10-190.GF60

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.