PC LEXAN™ EXL9132 SABIC INNOVATIVE JAPAN

217

Đặc tính:
Dòng chảy cao
Độ dẻo ở nhiệt độ thấp
Thời gian hình thành ngắn
Lĩnh vực ứng dụng:
Ứng dụng điện tử
Ứng dụng hàng không vũ tr
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	60 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	25 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	560 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	730 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	20 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	55 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	NoBreak
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	67.9 J

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	5VA
Burning wire flammability index	Burning wire flammability index 1.0mm	IEC 60695-2-12	960 °C
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	40 %
Hot filament ignition temperature	Hot filament ignition temperature 1.0mm	IEC 60695-2-13	825 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	95.1 Mpa
elongation	elongation Break	ASTM D638	100 %
Tensile strain	Tensile strain Yield	ISO 527-2/50	5.0 %
elongation	elongation Yield	ASTM D638	5.8 %
bending strength	bending strength	ISO 178	88.0 Mpa
Bending modulus	Bending modulus	ISO 178	2300 Mpa
Bending modulus	Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	2340 Mpa
Tensile strain	Tensile strain Break	ISO 527-2/50	100 %
Tensile modulus	Tensile modulus	ASTM D638	2270 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	2200 Mpa
tensile strength	tensile strength Yield	ASTM D638	58.1 Mpa
	tensile strength	tensile strength Yield	ISO 527-2/50	59.0 Mpa
		tensile strength	tensile strength Break	ASTM D638	58.5 Mpa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	55.0 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature	ASTM D152510	143 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	143 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	144 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	124 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	124 °C
		Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	136 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	136 °C
RTI Str	RTI Str	UL 746	50.0 °C
RTI Imp	RTI Imp	UL 746	50.0 °C
RTI Elec	RTI Elec	UL 746	130 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to80°C	ISO 11359-2	7.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	7.2E-05 cm/cm/°C
Ball Pressure Test	Ball Pressure Test 125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	7.2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to80°C	ISO 11359-2	7.5E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.18 g/cm³
density	density	density	ISO 1183	1.19 g/cm³
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.15 %
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ASTM D1238	17 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/1.2kg	ISO 1133	16.0 cm3/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.40-0.80 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD：3.20mm	Internal Method	0.40-0.80 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.35 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 50Hz	IEC 60250	4E-04
Relative permittivity	Relative permittivity 1MHz	IEC 60250	2.70
	Relative permittivity	Relative permittivity 60Hz	IEC 60250	2.70
	Relative permittivity	Relative permittivity	Relative permittivity 50Hz	IEC 60250	2.70
Dielectric strength	Dielectric strength 3.20mm,in Oil	IEC 60243-1	19 KV/mm
Dissipation factor	Dissipation factor 60Hz	IEC 60250	4E-04
Dissipation factor	Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.010
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 3

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test H358/30	ISO 2039-1	95.0 Mpa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

H358/30

ISO 2039-1

95.0 Mpa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.