mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	93.0 Mpa
Bending modulus	Bending modulus	ISO 178	2510 Mpa
elongation	elongation Break	ISO 527-2/5	> 50 %
	elongation	elongation Break4	ASTM D638	> 100 %
		elongation	elongation Break5	ASTM D638	> 100 %
			elongation	elongation Yield	ISO 527-2/50	4.4 %
				elongation	elongation Yield	ISO 527-2/5	4.3 %
					elongation	elongation Yield4	ASTM D638	4.3 %
					elongation	elongation	elongation Yield5	ASTM D638	4.2 %
tensile strength	tensile strength Break	ISO 527-2/50	45.0 Mpa
	tensile strength	tensile strength Break	ISO 527-2/5	51.0 Mpa
		tensile strength	tensile strength Break4	ASTM D638	56.0 Mpa
			tensile strength	tensile strength Break5	ASTM D638	66.0 Mpa
				tensile strength	tensile strength Yield	ISO 527-2/50	60.0 Mpa
					tensile strength	tensile strength Yield	ISO 527-2/5	62.0 Mpa
						tensile strength	tensile strength Yield5	ASTM D638	59.0 Mpa
						tensile strength	tensile strength	tensile strength Yield4	ASTM D638	63.0 Mpa
Tensile modulus	Tensile modulus --	ISO 527-2/1	2520 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --3	ASTM D638	2590 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
Mold temperature	Mold temperature	50 to 70 °C
drying temperature	drying temperature	80 to 90 °C
drying time	drying time	2.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
Hopper temperature	Hopper temperature	60 to 80 °C
Temperature at the rear of the barrel	Temperature at the rear of the barrel	200 to 230 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	220 to 260 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	230 to 270 °C
Spray nozzle temperature	Spray nozzle temperature	220 to 260 °C
Processing (melt) temperature	Processing (melt) temperature	230 to 270 °C

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	99.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	88.0 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	111 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	102 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	104 °C
Ball Pressure Test	Ball Pressure Test 73 to 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -30 to 80°C	ISO 11359-2	6.9E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -30 to 80°C	ISO 11359-2	7.1E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : 23 to 80°C	ISO 11359-2	7.5E-5 cm/cm/°C
RTI Elec	RTI Elec	UL 746	90.0 °C
RTI Imp	RTI Imp	UL 746	90.0 °C
RTI	RTI	UL 746	90.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Outdoor applicability	Outdoor applicability	UL 746C	f1
Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	0.20 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation, 23°C	ISO 62	0.60 %
Shrinkage rate	Shrinkage rate Flow	Internal Method	0.40 - 0.60 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 260°C/2.16 kg	ISO 1133	13.0 cm3/10min

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index	UL 746	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	V

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Compared to the anti leakage trace index

UL 746

PLC 0

Compared to the anti leakage trace index

IEC 60112

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.