mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus --2	ASTM D638	2680 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1	2680 Mpa
tensile strength	tensile strength Yield3	ASTM D638	65.0 Mpa
	tensile strength	tensile strength Yield4	ASTM D638	60.0 Mpa
		tensile strength	tensile strength Yield	ISO 527-2/5	61.0 Mpa
			tensile strength	tensile strength Yield	ISO 527-2/50	66.0 Mpa
				tensile strength	tensile strength Break4	ASTM D638	49.0 Mpa
					tensile strength	tensile strength Break3	ASTM D638	47.0 Mpa
						tensile strength	tensile strength Break	ISO 527-2/5	46.0 Mpa
						tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	47.0 Mpa
elongation	elongation Yield4	ASTM D638	4.0 %
	elongation	elongation Yield3	ASTM D638	4.0 %
		elongation	elongation Yield	ISO 527-2/5	4.0 %
			elongation	elongation Break4	ASTM D638	58 %
				elongation	elongation Break3	ASTM D638	31 %
					elongation	elongation Break	ISO 527-2/5	50 %
					elongation	elongation	elongation Break	ISO 527-2/50	21 %
Bending modulus	Bending modulus	ISO 178	2720 Mpa
bending strength	bending strength	ISO 178	97.0 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	80 to 90 °C
drying time	drying time	2.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
Hopper temperature	Hopper temperature	60 to 80 °C
Temperature at the rear of the barrel	Temperature at the rear of the barrel	200 to 230 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	220 to 260 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	230 to 270 °C
Spray nozzle temperature	Spray nozzle temperature	220 to 260 °C
Processing (melt) temperature	Processing (melt) temperature	230 to 270 °C
Mold temperature	Mold temperature	50 to 70 °C

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span	ISO 75-2/Bf	90.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span	ISO 75-2/Af	81.0 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	96.0 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	98.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ISO 11359-2	6.3E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40°C	ISO 11359-2	6.3E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 260°C/2.16 kg	ISO 1133	30.0 cm3/10min

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Melt Volume Flow Rate (MVR)

260°C/2.16 kg

ISO 1133

30.0 cm3/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.