mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638/ISO 527	34 kg/cm²(MPa)[Lb/in²]
tensile strength	tensile strength	ASTM D638/ISO 527	47 kg/cm²(MPa)[Lb/in²]
elongation	elongation	ASTM D638/ISO 527	30 %
Bending modulus	Bending modulus	ASTM D790/ISO 178	2.2 kg/cm²(MPa)[Lb/in²]
bending strength	bending strength	ASTM D790/ISO 178	76 kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength	Charpy Notched Impact Strength	ASTM D256/ISO 179	21 kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength	ASTM D256/ISO 179	10 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ASTM D256/ISO 179	19 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ASTM D256/ISO 179	9 kg·cm/cm(J/M)ft·lb/in

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature HDT	ASTM D648/ISO 75	98 ℃（℉）
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature HDT	ASTM D648/ISO 75	83 ℃（℉）
Vicat softening temperature	Vicat softening temperature	ASTM D1525/ISO R306	104 ℃（℉）
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	ASTM D696/ISO 11359	8.6×10-5 mm/mm.℃
Vickers softening temperature	Vickers softening temperature 1 Kg,50℃/hr	ISO 306	104 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa Unannealed	ISO 75/A	83 °C
linear expansion coefficient	linear expansion coefficient	ISO 11359	8.6 x 10-5
Flame Rating	Flame Rating 1.5mm	UL -94	HB

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792/ISO 1183	1.05
Shrinkage rate	Shrinkage rate	ASTM D955	0.4-0.7 %
melt mass-flow rate	melt mass-flow rate	ASTM D1238/ISO 1133	18 g/10min
Tensile strength, 50 mm/min, yield	Tensile strength, 50 mm/min, yield	ISO 527	47 Mpa
Melt index	Melt index 220℃×10KG	ISO 1133	18 ml/10 min
Molding shrinkage rate	Molding shrinkage rate	ISO 294-4	0.4-0.7 %
Elongation at Break	Elongation at Break 50 mm/min, break	ISO 527	30 %
bending strength	bending strength	ISO 178	76 Mpa
Bending modulus of elasticity	Bending modulus of elasticity	ISO 178	2.2 GPa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23 ℃ Notched	ISO 180/1A	19
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30℃ Notched		KJ/m2
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃ Notched	ISO 179	21 kJ/m²

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.