impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ASTM D4812	620 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C6	ISO 180/1U	42 kJ/m²
Dart impact	Dart impact 23°C, Energy at Peak	ASTM D3763	3.00 J
Dart impact	Dart impact	Dart impact --	ISO 6603-2	1.00 J

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus --1	ASTM D638	1830 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1	2020 Mpa
tensile strength	tensile strength Yield2	ASTM D638	43.0 Mpa
	tensile strength	tensile strength Yield	ISO 527-2/5	39.0 Mpa
		tensile strength	tensile strength Break2	ASTM D638	43.0 Mpa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2/5	39.0 Mpa
elongation	elongation Yield2	ASTM D638	14 %
	elongation	elongation Yield	ISO 527-2/5	22 %
		elongation	elongation Break2	ASTM D638	30 %
		elongation	elongation	elongation Break	ISO 527-2/5	43 %
Bending modulus	Bending modulus 50.0 mm Span3	ASTM D790	2020 Mpa
Bending modulus	Bending modulus	Bending modulus --4	ISO 178	2080 Mpa
bending strength	bending strength --	ISO 178	60.0 Mpa
bending strength	bending strength	bending strength Break, 50.0 mm Span3	ASTM D790	63.0 Mpa
Friction coefficient	Friction coefficient Dynamic	ASTM D3702	0.25
Friction coefficient	Friction coefficient	Friction coefficient Static	ASTM D3702	0.14
Wear factor	Wear factor	ASTM D3702	1.8E+6 10^-8 mm³/N·m

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	80 °C
drying time	drying time	4.0 hr
Temperature at the rear of the barrel	Temperature at the rear of the barrel	175 to 190 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	195 to 205 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	210 to 220 °C
Processing (melt) temperature	Processing (melt) temperature	200 to 215 °C
Mold temperature	Mold temperature	80 to 110 °C
Back pressure	Back pressure	0.200 to 0.300 Mpa
Screw speed	Screw speed	30 to 60 rpm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	87.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span6	ISO 75-2/Af	79.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ASTM E831	1.1E-4 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40 to 40°C	ASTM E831	1.1E-4 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate Flow : 24hr	ASTM D955	2.1 - 2.9 %
Shrinkage rate	Shrinkage rate	Shrinkage rate Across FlowFlow : 24hr	ASTM D955	2.1 - 2.9 %
Water absorption rate	Water absorption rate 24 hr, 50% RH	ASTM D570	0.18 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	0.43 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.