PA66 POLYNIL® P36/4 Celanese Corporation

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	4.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	5.5 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/A	4.5 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/A	5.5 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	V-2
Burning wire flammability index	Burning wire flammability index 0.8mm	IEC 60695-2-12	750 °C
Burning wire flammability index	Burning wire flammability index	Burning wire flammability index 3.2mm	IEC 60695-2-12	850 °C
Hot filament ignition temperature	Hot filament ignition temperature 0.8mm	IEC 60695-2-13	775 °C
Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 3.2mm	IEC 60695-2-13	750 °C
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	28 %
UL flame retardant rating	UL flame retardant rating 3.2mm	UL 94	V-2

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus 23°C	ISO 527-2	3100 MPa
tensile strength	tensile strength Yield,23°C	ISO 527-2	81.0 MPa
Tensile strain	Tensile strain Break,23°C	ISO 527-2	50 %
Bending modulus	Bending modulus 23°C	ISO 178	2850 MPa
bending strength	bending strength 23°C	ISO 178	120 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	225 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	72.0 °C
Continuous use temperature	Continuous use temperature	IEC 60216	85.0 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B	240 °C
Ball Pressure Test	Ball Pressure Test 125°C	IEC 60695-10-2	通过
	Ball Pressure Test	Ball Pressure Test 165°C	IEC 60695-10-2	通过
	Ball Pressure Test	Ball Pressure Test	Ball Pressure Test Melting Temperature	IEC 60695-10-2	258 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density 23°C	ISO 1183	1.14 g/cm³
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	1.5 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	8.5 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

density

23°C

ISO 1183

1.14 g/cm³

Water absorption rate

23°C,24hr

ISO 62

1.5 %

Water absorption rate

Saturation,23°C

ISO 62

8.5 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dielectric strength	Dielectric strength 2.00mm	IEC 60243-1	18 kV/mm
Compared to the anti leakage trace index	Compared to the anti leakage trace index 3.20mm,SolutionA	IEC 60112	PLC 0

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Dielectric strength

2.00mm

IEC 60243-1

18 kV/mm

Compared to the anti leakage trace index

3.20mm,SolutionA

IEC 60112

PLC 0

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.